FeCrAl Alloy Heating Resistance Wire 0.02-10mm Diameter High-Temperature

Price Negotiable

Price: USD5-6/kg

MOQ: 10kg

Delivery Time: 10-15Days

Brand: tankii

Product Description

Fecral Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire

Product Specifications

Attribute	Value
Diameter	0.02-10mm
Surface	Oxidation, bright

Product Description

This high-temperature heating resistance wire is manufactured using powder metallurgy technology with refined master alloy as raw material. Through special cold and hot processing along with heat treatment processes, the product achieves exceptional performance characteristics.

Key Advantages:

Strong oxidation resistance
Excellent high-temperature corrosion resistance
Minimal electrothermal component creep
Extended service life at high temperatures
Stable resistance characteristics

Suitable for extreme environments including temperatures up to 1420°C, high power density applications, corrosive atmospheres, and carbon-rich conditions. Ideal for use in:

Ceramic kilns
High-temperature heat treatment furnaces
Laboratory furnaces
Electronic industrial furnaces
Diffusion furnaces

Material Composition

Element	Min (%)	Max (%)
C	-	0.04
Si	-	0.5
Mn	-	0.4
Cr	20	22
Al	5.5	6.0
Fe	Bal.	Bal.

Mechanical & Thermal Properties

Tensile Strength at Room Temperature	650-750MPa
Elongation Rate	15-25%
Hardness	HV220-260
Density	7.1g/cm³
Tensile Strength at 1000°C	22-27MPa
High Temperature Durability (1000°C at 6MPa)	≥100h
Resistivity	1.45×10^-6 Ω.m
Melting Point	1500°C
Maximum Continuous Working Temperature	1400°C