Epoxy Resin Tooling Paste for Mold Manufacturing - 40mm Layer Thickness, 70-75°C Temperature Resistance
Price:
Negotiation
MOQ:
200kgs
Delivery Time:
15 Days
Brand:
LH-tool®
Product Description
Product Overview
This two-component epoxy resin tooling paste is formulated for high dimensional accuracy in mold manufacturing applications. Available in 10kg, 15kg, and 20kg packaging options, this beige-colored material offers excellent machining performance with maximum layer thickness of 40mm.
Key Applications
- Wind power blade molds, cabin cover molds, and automotive master models
- Sheet metal forming molds, tensile modulus, and bending molds
- Foaming molds, vacuum forming molds, and injection molds
- Composite materials forming molds and rapid prototyping
- Foundry industry applications including sand core boxes and checking fixtures
Technical Specifications
| Material | 5200A | 5200B | Mixed |
|---|---|---|---|
| Description | Epoxy Resin | Curing Agent | |
| Mixing Ratio | 1 | 1 | |
| Color | Brown | Yellow | Brown |
| Mixed Time (500g, 25°C) | 30 min | ||
| Curing Time Before Machining (20-25mm) | 6-8 hours | ||
| Maximum Layer Thickness | 40 mm | ||
| Density | 0.7-0.8 g/cm³ | ||
| Hardness (Shore D) | 65-70 | ||
| Temperature Resistance | 70-75°C | ||
| Coefficient of Thermal Expansion | 45-50 ×10⁻⁶ K⁻¹ | ||
| Compressive Strength | 52 N/mm² | ||
| Flexural Strength | 32 N/mm² | ||
| Tensile Strength | 26 N/mm² | ||
| Package Size | 10 kg | 10 kg |
Material Characteristics
- Excellent machining performance (milling, planing, cutting, drilling)
- Fine surface structure and easy finishing
- High dimensional stability and accuracy
- Non-toxic and environmentally friendly
- Low heat generation during curing
- Odor-free during application and processing
- Easy to shape, repair, and modify
- Reduces overall mold manufacturing costs
Application Process
Mix components thoroughly in 1:1 ratio until uniform color is achieved. Use vacuum mixer to minimize bubbles. Apply in layers not exceeding 40mm thickness. Allow proper curing (80°C for 8 hours or 3 days at room temperature) before machining. Use release agents for metal and composite structures.
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Yongzhou Lihong New Material Co.，Ltd
Location
No ,2 Hengsan Road, Circular Economy Industrial Park, Wenmiao Street ,Ningyuan County, Yongzhou City, Hunan Province, China
Contact Person
Rolland