Brown Epoxy Resin Tooling Paste for Mold Making

High-performance two-component epoxy resin system designed for creating master models, prototypes, and molds with excellent surface finish and machining characteristics.

Key Features

Easy shaping and machining capabilities
Fine surface structure for detailed reproduction
Single coating thickness up to 40mm
Low reaction heat generation during curing
Odor-free application and processing
Excellent dimensional stability
Room temperature curing with good machining performance

Applications

Yacht and benchmark model creation
System and sand-cast models
Rapid prototyping applications
Master model production

Technical Specifications

Material	5200A	5200B	Mixed
Description	Epoxy Resin	Curing Agent
Mixing Ratio	1	1
Color	Brown	Yellow	Brown
Mixed Time (500g, 25°C)			30 min
Curing Time Before Machining			6-8 hours
Maximum Layer Thickness			40 mm
Density			0.7-0.8 g/cm³
Hardness (Shore D)			65-70
Temperature Resistance			70-75°C
Coefficient of Thermal Expansion			45-50 × 10⁻⁶ K⁻¹
Compressive Strength			52 N/mm²
Flexural Strength			32 N/mm²
Tensile Strength			26 N/mm²
Package Size	10 kg	10 kg

Application Instructions

Mix components thoroughly in 1:1 ratio until uniform brown color is achieved
Use vacuum mixer to minimize bubble formation
Apply single coating layers not exceeding 40mm thickness
Allow complete curing between layers if multiple applications are needed
For optimal machining performance: rough machining after room temperature curing, precision work after 3 days
Use mold release agents when working with metal or composite structures
Ensure proper support frame strength and stability during processing