Titanium Ti Pellets Evaporation Materials
Titanium Ti Pellets Evaporation Materials
Titanium Pellets are a silver-white metal with many excellent properties. With a density of 4.54 g/cm3, titanium is 43% lighter than steel and slightly heavier than the famous light metal magnesium. Its mechanical strength is twice that of steel, five times that of aluminum, and five times that of magnesium. Titanium can withstand high temperatures. Its melting point is 1942K, which is nearly 1000K higher than gold and 500K higher than steel.
Chemical Composition of Titanium Pellets
| Grade | N | C | H | Fe | O | Al | V | Pa | Mo | Ni | Ti |
| Gr1 | 0.03 | 0.08 | 0.015 | 0.2 | 0.18 | / | / | / | / | / | bal |
| Gr2 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / | / | / | bal |
| Gr3 | 0.05 | 0.08 | 0.015 | 0.3 | 0.35 | / | / | / | / | / | bal |
| Gr5 | 0.05 | 0.08 | 0.015 | 0.4 | 0.2 | 5.5~6.75 | 3.5~4.5 | / | / | / | bal |
| Gr7 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | 0.12~0.25 | / | / | bal |
| Gr9 | 0.03 | 0.08 | 0.015 | 0.25 | 0.15 | 2.5~3.5 | 2.0~3.0 | / | / | / | bal |
| Gr12 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / | 0.2~0.4 | 0.6~0.9 | bal |
Tensile Requirements of Titanium Pellets
| Grade | Tensile Strength (min) | Yield strength 0.2%Offset | Elongation in 2in.Or 50mm % (min) | ||
| Min | |||||
| KSI | MPA | KSI | MPA | ||
| Gr1 | 35 | 240 | 20 | 138 | 20 |
| Gr2 | 50 | 345 | 40 | 275 | 18 |
| Gr3 | 65 | 450 | 55 | 380 | 18 |
| Gr5 | 130 | 895 | 120 | 828 | 10 |
| Gr7 | 50 | 345 | 40 | 275 | 18 |
| Gr12 | 70 | 483 | 50 | 345 | 18 |
Application of Titanium Pellets
Titanium billets have the characteristics of heat resistance, corrosion resistance, high strength, low density, and good biocompatibility. They are widely used in fields such as aerospace, chemical engineering, nuclear energy, and sports. It is also one of the main structural materials for modern aircraft and engines.