PFC-20 Fabric Reinforced Phenolic Wear Ring - 1.2-1.4 g/cm³ Density, -40°C to +130°C Temperature Range
Price:
Negotiable
MOQ:
1pcs
Delivery Time:
25-30 working days
Brand:
Joyreap
Product Description
Fabric Reinforced Phenolic Wear Ring Overview
PFC-20 high-strength fabric reinforced phenolic guide rings are manufactured using solvent phenolic resin with uniformly dispersed graphite and premium cotton fiber. The material undergoes a heat solidification process under controlled pressure and temperature conditions, resulting in exceptional mechanical properties and durability for demanding industrial applications.
Material Composition
High-strength phenolic resin with graphite reinforcement and high-quality cotton fiber
Performance Advantages
- High mechanical strength with tensile strength ≥40 MPa
- Excellent abrasion resistance for extended service life
- Superior temperature resistance from -40°C to +130°C
- Capable of sustaining strong vibration under semi-static conditions
- Resistant to impact loads and slight torque loads
- Operates effectively with minimal or no lubrication
Industrial Applications
- Ball valves and butterfly valve bushings
- Plastic mechanical guide sleeves
- Bushings for water conservation projects
- Guide sleeves for vertical pillars of hydraulic machinery and forging presses
- Bushings for supporting frames of engineering machinery and vehicle pivot axles
- Marine engineering equipment spherical bearings and marine bearing materials
Technical Specifications
| Specification | Color | Density (g/cm³) | Tensile Strength | Compressive Strength | Hardness | Coefficient of Friction | Temperature Range |
|---|---|---|---|---|---|---|---|
| PFC-20 | Black | 1.2-1.4 | ≥40 MPa | ≥160 MPa | 90-100 | Dry: 0.15-0.3 Oil: 0.1-0.12 |
-40°C to +130°C |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Jiaxing Joyreap Precision Machinery Co.,Ltd
Location
No 168 Kapa Road Dayun Town Jiashan Zhejiang China
Contact Person
Catherine Hu