ASTM B111 ASME SB111 C68700 Aluminum Brass Tube For Heat Exchanger
ASTM B111 ASME SB111 C68700 Aluminum Brass Tube for Heat Exchanger
Description
It has high strength and hardness, good plasticity, and can be processed under pressure in cold and hot states. It has good corrosion resistance to seawater and brine, and resistance to impact corrosion, but it has the tendency of dezincification and corrosion rupture. Used for ships and other condensing pipes and other corrosion-resistant parts.
Chemical Composition
|
Mechanical Properties
| Copper or Copper Alloy UNS NO. | Temper Designation | Tensile Strength | Yield Strength | Elongation in 2 in., |
|
| Code | Former | min ksi(min MPa) | min ksi(min MPa) | min % | |
| C68700 | O61 | annealed | 50(345) | 18(125) | --- |
Equivalent Grade of C68700
| Material Designation | Corresponding Material Symbol | ||||
| GB/T8890 | ASTM B111 | BS2871 | JIS H3300 | DIN1785 | |
| Aluminums Brass | HAL77-2 | C68700 | CZ110 | C6870 | CuZn20Al2 |
| Standard | BS 2871 PART3 | ASTM B 111 | DIN 1785 | NFA 51 102 | JIS H3300 | IS 1545 |
| Symbol | CZ 110 | C 68700 | CuZn20AI2 | CuZn22AI2 | C 6870 | CuZn21AI2As |
| Cu | 76.0-78.0 | 76.0-79.0 | 76.0-79.0 | 76.0-79.0 | 76.0-79.0 | 76.0-78.0 |
| Al | 1.8-2.3 | 1.8-2.5 | 1.8-2.3 | 1.8-2.5 | 1.8-2.5 | 1.8-2.3 |
| Pb | 0.07 | 0.07 | 0.07 | 0.07 | 0.07 | 0.07 |
| Ni | - | - | 0.1 | - | - | - |
| Fe | 0.06 | 0.06 | 0.07 | 0.06 | 0.06 | 0.06 |
| Zn | REM'DER | REM'DER | REM'DER | REM'DER | REM'DER | REM'DER |
| As | 0.02-0.06 | 0.02-0.06 | 0.02-0.35 | 0.02-0.06 | 0.02-0.06 | 0.02-0.06 |
| P | - | - | 0.01 | - | - | - |
| Total Impurities Max. | - | |||||
| 0.03 | - | 0.1 | 0.3 | - | 0.3 | |
| Condition | M | 61 | F39 | - | O | O |
| TA | - | F34 | - | - | TA | |
| O | - | - | - | - | D | |
| Yield Strength n/mm2 | - | 125 | 1 50-230 | - | - | 400Mpa Max. |
| - | 105 | 120-180 | - | - | 355Mpa Min. | |
| - | - | - | - | - | 415Map | |
| Tensile n/mm2 Minimum | - | 345 | 390 | - | 373 | - |
| - | - | 340 | - | - | - | |
| Elng'Tion Percent (%) | - | - | 45Min. | - | 40Min. | 85Max. |
| - | - | 55Min. | - | - | 80-110 | |
| - | - | - | - | - | 130Min. | |
| Hardness HV5 - | 150Min | - | - | 80-130 | - | - |
| 85-110 | - | - | - | - | - | |
| 75Max. | - | - | - | - | - | |
| Grain Size mm (75X) | 0.05Max. | 0.010-0.045 | - | 0.010-0.045 | 0.010-0.045 | 0.010-0.045 |
Characteristic
A Copper Zinc Alloy containing tin and small amount of Arsenic, which is added as an inhibitor against dezincification.
The pressure of Tin imparts to the alloy good corrosion resistance in a moderately polluted river water and clean seawater, either stagnant or slow moving (upto about 2 mtrs/sec.). The most common and wrought form is tube for heat exchange equipment. Guide to the selection of tube material:Clear river, Lake or Canal Water.a.
Dissolved salts more than 2000 ppm.b. Chloride less then 20 ppm.c. H2S and Ammonia is less than 1 ppm.d. Suspended solids less than 25 ppm.e. For temperature more than 2000C and less than 4500 C.Permissible average velocity of water 1.8-2.0 meters/sec.
Application
- Heat Exchangers
- Refineries
- Power Plants
- Desalination Plants
- Ship Building & Ship Repairs
- Condensers
- Ferrules
- Distillers