DIN 17660 CuZn20Al2 Copper Alloy Seamless Tube Condenser Heat Exchanger
DIN 17660 CuZn20Al2 Copper Alloy Seamless Tube Condenser Heat Exchanger
CuZn20 ordinary brass has high strength, good plasticity, and high corrosion resistance, and is used for thin-walled pipes, corrugated pipes, paper mesh, and building materials. Tensile strength σ B (MPa): ≥ 265, Hot working temperature 820~870 ℃; Annealing temperature: 600-700 ℃; The low-temperature annealing temperature for relieving internal stress is 260 ℃.
DIN 17660 CuZn20Al2 Copper Alloy Seamless Tube
| Al(%) | Mn(%) | Pb(%) | Fe(%) | Ni(%) | Zn(%) | Cu(%) |
|---|---|---|---|---|---|---|
| 1.8-2.3 | ≦0.1 | ≦0.07 | ≦0.07 | ≦0.1 | ≧15 | 76.0-79.0 |
DIN 17660 Other Grades Or Similar Grades
| Grade | Standard | Area | Content |
|---|---|---|---|
| CuZn 44 Pb 2 | DIN 17660 | Germany | Wrought copper alloys; copper-zinc alloys (brass); (special brass); chemical composition |
| CuZn35Ni2 | DIN 17660 | Germany | Wrought copper alloys; copper-zinc alloys (brass); (special brass); chemical composition |
| CuZn 40 Al 2 | DIN 17660 | Germany | Wrought copper alloys; copper-zinc alloys (brass); (special brass); chemical composition |
| 2.0360 | DIN 17660 | Germany | Wrought copper alloys; copper-zinc alloys (brass); (special brass); chemical composition |
| CuZn 15 | DIN 17660 | Germany | Wrought copper alloys; copper-zinc alloys (brass); (special brass); chemical composition |
| 2.0240 | DIN 17660 | Germany | Wrought copper alloys; copper-zinc alloys (brass); (special brass); chemical composition |
| Standard Grade | ASTM B 111 C68700 |
EN 12451 CuZn20Al2As |
DIN 17660/1785 CuZn20Al2 |
BS 2871 CZ 110 |
JIS H3300 C6870 |
GB/T8890 HAL77-2 |
| Cu | 76.0-79.0 | 76.0-79.0 | 76.0-79.0 | 76.0-78.0 | 76.0-79.0 | 76-79 |
| Al | 1.8-2.5 | 1.8-2.3 | 1.8-2.3 | 1.8-2.3 | 1.8-2.5 | 1.8-2.5 |
| Fe | 0.06 max | 0.07 max | 0.07 max | 0.06 max | 0.06 max | 0.06 max |
| Pb | 0.07 max | 0.05 max | 0.07 max | 0.07 max | 0.07 max | 0.03 max |
| Zn | Bal. | Bal. | Bal. | Bal. | Bal. | Bal. |
| As | 0.02-0.10 | 0.02-0.06 | 0.02-0.035 | 0.02-0.06 | 0.02-0.06 | 0.03-0.06 |
| P | - | 0.01 max | 0.01 max | - | - | 0.02 max |
| Mn | - | 0.1 max | 0.1 max | - | - | - |
| Total impurities | - | 0.3 max | 0.1 max | 0.3 max | - | 0.3 max |
|
Condition |
O61 | R390 | F39 | M | O | M |
| - | R340 | F34 | TA | - | Y2 | |
| - | - | O | - | - | ||
| Yield Strength N/mm2 |
125 min | 150 min | 150-230 | - | - | - |
| - | 120 min | 120-180 | - | - | - | |
| - | - | - | - | - | - | |
| Tensile Strength N/mm2 |
345 min. | 390 min | - | - | 373 min | 370 min |
| - | 340 min | - | - | - | 350 min | |
| - | - | - | - | - | - | |
| Elongation (%) | - | 45 min | 45 min | - | 40 min | 40 min |
| - | 55 min | 55 min | - | - | 50 min | |
| - | - | - | - | - | - | |
| Hardness Hv5 | - | - | - | 150 min | - | - |
| - | - | - | 85-110 | - | - | |
| - | - | - | 75 max | - | - | |
|
Typical use
|
Most used copper alloy for heat exchanger tubes application. |
|||||