The Autoclaved Aerated Concrete (AAC) material was developed in 1924 in Sweden. It has become one of the most used building materials in Europe and is rapidly growing in many other countries around the world.

Autoclaved Aerated Concrete, also known as Aircrete, is a lightweight, load-bearing, high-insulating, durable building product, which is produced in a wide range of sizes and strengths.

AAC offers incredible opportunities to increase building quality and at the same time reduce costs at the construction site. AAC is produced out of a mix of quartz sand and/or pulverised fly ash (PFA), lime, cement, gypsum/anhydrite, water and aluminium and is hardened by steam-curing in autoclaves. As a result of its excellent properties, AAC is used in many building constructions, for example in residential homes, commercial and industrial buildings, schools, hospitals, hotels and many other applications.

Autoclaved aerated concrete is actually hydrated calcium silicate. The calcium is obtained from quick lime, hydrated lime and cement. The gypsum is used as a catalyst and for optimizing the properties of AAC.

The silica is obtained from silica sand, fly ash (PFA), crushed silica rock and/or stone. It is possible to obtain silica as a by-product from other processes, e.g. foundry sand or burgee from glass grinding, provided the levels of alkalis or other impurities are not too high.

This product is key equipment which has a widely application in building material factory to autoclaved cure different kinds of building materials. It is also used in areas of chemical, textile, wood, metallurgy, military industry. Convenient operation, security and reliable are its advantages.

AAC BLOCK PRODUCTION LINE RAW MATERIAL INTODUCTION

AAC block machine main material:coal ash sand waste mine material coal stonestone dust and other silicon materials.

1 Product weight is according to 600kg/m3 to control.

2 annual capacity 200,000M3.

3 set raw material proportion: cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum paste powder 350g/M3.

4 water and material rate 0.631

5 one mould product 2.88M3

6 Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.

7 casting slurry temperature 38-42 degree

8 body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa

9 Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.