Fire Resistant Refractory Cement Powder For Boiler
China fire resistant high heat refractory cement for boiler
The raw materials of calcium aluminate cement CA-70/80 are high purity calcium materials and high pure alumina. The raw materials should be mixed according to suitable ratio. The raw material should be burned to partly fuse. After cooling, α-Al2O3 powder added into clinker, then ground to cement. The content of Al2O3 is usually controlled within 68% to 72%. The principal compounds of it are CA and CA2.
| Product | CA-65 | CA-68 | CA-70 | CA-75 | CA-80 | |
| Chemical Composition (%) | Al2O3 | 64-66 | 67-69 | 69-71 | 73-75 | 77-80 |
| CaO | 32-34 | 29-31 | 27-29 | 23-25 | 18-20 | |
| SiO2 | 1.8 | 1.2 | 0.3 | 0.3 | 0.3 | |
| Fe2O3 | 0.6 | 0.6 | 0.3 | 0.3 | 0.3 | |
| Specific Surface (cm2/g) | 4500 | 4500 | 5000 | 5500 | 7000 | |
| Setting time (h:min) | Initial setting (min) | 0:40 | 0:40 | 0:40 | 0:45 | 0:45 |
| Final Setting (min) | 8:00 | 8:00 | 10:00 | 10:00 | 10:00 | |
| Cold Modulus of Rupture (MPa) | 24 hour | 6.0min | 6.0min | 6.0min | 6.0min | 5.0min |
| 72 hour | 8.0min | 8.0min | 8.0min | 8.0min | 6.0min | |
| Cold Crushing Strength (Mpa) | 24hour | 45.0min | 45.0min | 45.0min | 45.0min | 35.0min |
| 72hour | 70.0min | 70.0min | 70.0min | 70.0min | 60.0min | |
| Refractoriness (°C) | 1680 | 1710 | 1730 | 1750 | 1770 | |
Calcium aluminate CA-70/80 is used for manufacturing good property (low water, low cement) refractory castable, or unshaped bulk refractory materials, which are used in high temperature, high pressure, and reducing condition. It is also high quality binder of refractory castable, which is extensively applied in chemical industry, metallurgical industry, building material, petroleum industry, ceramic industry etc.