Hot Rolled SAE4140 Alloy Steel Round Bar OD 200-600mm SCM440 Forged Solid Rod
Hot Rolled SAE4140 Alloy Steel Round Bar OD 200-600mm SCM440 Forged Solid Rod
1: AISI 4140 steel introduction
AISI 4140 is defined as a low alloy steel which has 1% Cr-Mo as strengthening alloy elements.Compared with AISI 4130, it has a higher carbon content with good balance of strength, toughness ,abrasion and impact resistance and heat treatment capabilities,but poor in weldability characteristics.AISI 4140 is generally supplied in quenched and tempered condition with hardness 28-32HRC
2: AISI 4140 Steel equivalent
| Country | China | Japan | Germany | USA | British |
| Standard | GB/T 3077 | JIS G4105 | DIN (W-Nr.) EN 10250 |
AISI/ASTM ASTM A29 |
BS 970 |
| Grade | 42CrMo | SCM440 | 42crmo4/1.7225 | 4140 | EN19/709M40 |
3: AISI 4140 steel chemical composition
| Grade | C | Si | Mn | P | S | Cr | Mo | Ni |
| 42CrMo | 0.38-0.45 | 0.17-0.37 | 0.5-0.80 | ≤0.035 | ≤0.035 | 0.9-1.2 | 0.15-0.25 | - |
| SCM440 | 0.38-0.43 | 0.15-0.35 | 0.6-0.85 | ≤0.035 | ≤0.04 | 0.9-1.2 | 0.15-0.30 | - |
| 42crmo4/1.7225 | 0.38-0.45 | ≤ 0.4 | 0.6-0.9 | ≤0.025 | ≤0.035 | 0.9-1.2 | 0.15-0.30 | - |
| 4140 | 0.38-0.43 | 0.15-0.35 | 0.75-1.00 | ≤0.035 | ≤0.04 | 0.8-1.1 | 0.15-0.25 | - |
| EN19/709M40 | 0.35-0.45 | 0.15-0.35 | 0.5-0.80 | ≤0.035 | ≤0.035 | 0.9-1.5 | 0.2-0.40 | - |
4: AISI 4140 steel mechanical properties(for guidance only)
| Grade | Tensile strength σb(MPa) |
Yield strength σs (MPa) |
Elongation δ5 (%) |
Reduction ψ (%) |
Impact Value Akv (J) |
Hardness |
| 4140 | ≥1080 | ≥930 | ≥12 | ≥45 | ≥63 | 28-32HRC |
5: AISI 4140 steel overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm |
|
| Width 20mm-1000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
| Application | AISI 4140 steel finds many applications as forgings for the aerospace,oil and gas,automotive, agricultural and defense industries etc. Typical applications for 4140 steel uses include:forged gears,spindles,fixtures,jigs,collars,Axles,conveyor parts,crow bars,logging parts,shafts,sprockets,studs,pinions,pump shafts, rams, and ring gears etc |
|
6: Delivery condition
For hot forged or hot rolled bar, usually the delivery condition is hot forged or rolled, annealed, rough turned.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.
FAQ
1) why you chose us ?
Because we have large stocks and we have long term cooperative factories.
We can get the lowest ex-factory prices. The price are quite reasonable and it is lower than our commercial peers.
Also, we can guarantee the quality of our products.
2) Our minimum order quantity:
15 Metric Tons
3) How about the Delivery Time?
The steel pipe will be produced since we getting your deposit by T/T or original L/C, and delivery to the port of loading within 25~30 days.
For normal size, some stocks in our factory now, we can shipment within 7~10 days after receive the deposit.
4) What kind of payment does your company support?
T/T, 100% L/C at sight.
5) Do you charge for the samples?
No, we provide samples free, you pay for the freight charge.
6) Main market:
Mid East South America South Asia Africa Southeast Asia Northern Europe Western Europe etc.
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.