Haynes-188 GH5188 Stainless Steel Round Bar Haynes 188 Material Haynes 188 Forging Bar
Haynes-188 GH5188 Stainless Steel Round Bar Haynes 188 Material Haynes 188 Forging Bar
Alloy® 188 is a cobalt-base austenitic alloy with excellent high temperature strength and good oxidation resistance to 2000°F (1093°C). The high chromium level coupled with small additions of lanthanum produce an extremely tenacious and protective scale. The alloy also has good sulfidation resistance and excellent metallurgical stability displayed by its good ductility after prolonged exposure to elevated temperatures.
Alloy 188 is non-magnetic. It has good high temperature strength up to 1800ºF (982˚C) and good oxidation resistance up to 2100ºF (1149˚C). This alloy performs well in continuous high temperature service and has excellent oxidation, spalling and corrosion resistance, achieved through the addition of chromium in combination with a minute amount of lanthanum. The lanthanum addition produces a tenacious, protective oxide scale at high temperatures. This alloy also maintains its ductility at cryogenic temperatures but strength levels are increased substantially.
Standard Inventory Specifications
- UNS R30188
- AMS 5608
- AMS 5772
- B50TF74
- PWA-LCS
- GE-S400/1000
- RR SABRe Edition 2
- DFARS Compliant
- SAE AMS 5608
Common Trade Names
- Udimet Alloy 188 (® Special Metals )
- Haynes 188 Alloy (® Haynes International)
- ATI 188 (™ Allegheny Technologies)
Inventory Size Range
- Sheet : .020"-.083"
- Bar : 0.375" - 4.000"
Please contact us for more details.
The technical data provided is for information only and not for design purposes. It is not warranted or guaranteed.
| Element | Percent By Weight | |
|---|---|---|
| C | Carbon | 0.05 - 0.15% |
| Mn | Manganese | 1.25% max |
| Si | Silicon | 0.20 - 0.50% |
| Cr | Chromium | 20.0 - 24.0% |
| Ni | Nickel | 20.0 - 24.0% |
| W | Tungsten | 13.0 - 16.0% |
| La | Lanthanum | 0.02 - 0.12% |
| B | Boron | 0.015% max |
| Fe | Iron | 3% max |
| Co | Cobalt | Balance |
Common Applications of Alloy 188 Cobalt
- Gas turbine operations
- Combusters
- Flame holders
- Liners
- Transition ducts
- Exhaust frames
Alloy 188 Physical Properties
- Density 0.330 lb/in³ 9.14 g/cm³
- Melting Range 2375-2425 °F 1300-1330 °C
- Specific Heat 0.097 at 70 °F, Bru/lb °F 405 at 21 °C, J/kg °C
- Permeability 1.0007 at 200 oersted
- Coefficient of Expansion 6.6 0-200 °F, 10¯⁶ in/in●°F
- Thermal conductivity 84 Btu●in/ft²●h●°F W/wm●°C
- Electrical Resistivity 613 ohm●circ mil/ft 102.0 microhm-cm
Mechanical Properties and Yield Strength of Alloy 188
|
Yield Strength |
Tensile Strength |
Elongation |
||
|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % |
| 65 | 446 | 140 | 963 | 55 |