2 Inch SCH40 / 40S 2507 Super Duplex Stainless Steel Pipes ASTM A789 S32750 Duplex Steel Tube

Standards

ASTM/ASME:A240 - UNS S32750
EURONORM:1.4410 - X2 Cr Ni MoN 25.7.4
AFNOR:Z3 CN 25.06 Az
DIN/EN 1.4410,ASME SA-240

Duplex 2507 (UNS S32750) is a super duplex stainless steel with 25% chromium, 4% molybdenum, and 7% nickel designed for demanding applications which require exceptional strength and corrosion resistance, such as chemical process, petrochemical, and seawater equipment. The steel has excellent resistance to chloride stress corrosion cracking, high thermal conductivity, and a low coefficient of thermal expansion. The high chromium, molybdenum, and nickel levels provide excellent resistance to pitting, crevice, and general corrosion.

1. Products Details

Mittel  inventory now includes Duplex 2507, which is a super duplex stainless steel with 25% chromium, 4% molybdenum, and 7% nickel. This alloy is designed for applications which require exceptional strength and corrosion resistance; examples include applications in chemical processing, petrochemical, and seawater equipment. The steel has excellent resistance to chloride stress corrosion cracking, high thermal conductivity and a low coefficient of thermal expansion. The high chromium, molybdenum, and nickel levels provide excellent resistance to pitting, crevice, and general corrosion.

Chemical Properties

Mechanical Properties

1. 2507 duplex stainless steel pipe mechanical properties at room temperature

Pipe:thickness≤20mm ；δb/MPa:800-1000 ,δ0.2/MPa:≥550 ,δ5/%:≥25 ,(HV):290

2. 2507 duplex stainless steel plate in the mechanical properties of room temperature of -200 ℃ :

/℃ δb/MPa
Room Temperature ≥530
Sheet 100 ≥450
200 ≥400

3. Mechanical properties of 2507 large-diameter seamless tube

Dia*thickness δb/MPa δ0.2/MPa δ5/% (HV)
273.0mm×4.19mm 894 644 40 284
323.9mm×4.57mm 858 662 45 270
406.4mm×4.74mm 854 657 41 272

2. Processing

Hot forming
2507 should be hot worked between 1875°F and 2250°F. This should be followed by a solution anneal at 1925°F minimum and a rapid air or water quench.

Cold Forming
Most of the common stainless steel forming methods can be used for cold working 2507. The alloy has a higher yield strength and lower ductility than the austenitic steels so fabricators may find that higher forming forces, increased radius of bending, and increased allowance for springback are necessary. Deep drawing, stretch forming, and similar processes are more difficult to perform on 2507 than on an austenitic stainless steel. When forming requires more than 10% cold deformation, a solution anneal and quench are recommended.

Heat Treatment
2507 should be solution annealed and quenched after either hot or cold forming. Solution annealing should be done at a minimum of 1925°F. Annealing should be followed immediately by a rapid air or water quench. To obtain maximum corrosion resistance, heat treated products should be pickled and rinsed.

Welding
2507 possesses good weldability and can be joined to itself or other materials by shielded metal arc welding (SMAW), gas tungsten arc welding (GTAW), plasma arc welding (PAW), flux cored wire (FCW), or submerged arc welding (SAW). 2507/P100 filler metal is suggested when welding 2507 because it will produce the appropriate duplex weld structure.

Preheating of 2507 is not necessary except to prevent condensation on cold metal. The interpass weld temperature should not exceed 300°F or the weld integrity can be adversely affected. The root should be shielded with argon or 90% N2/10% H2 purging gas for maximum corrosion resistance. The latter provides better corrosion resistance.

3. Payment ,Shipping

Shipping:

Standard export package with water proof paper, and metal pallet, and angle bar protection, and steel strip or as required

20ft GP: 5.8m(length) x 2.13m(width) x 2.18m(high) about 24-26CBM, 23MTS

40ft GP: 11.8m(length) x 2.13m(width) x 2.18m(high) about 54CBM, 27MTS

40ft HG: 11.8m(length) x 2.13m(width) x 2.72m(high) about 68CBM, 27MTS

1. Are you a manufacturer or a trading company?
   We are a manufacturer for most sizes listed and can assist with the entire project package if in need.
2. Where are your plants located in China?
   By 2019, we have a carbon steel plant in Changzhou City and a stainless steel plant in wuxi City, with details available on our website.
3. Do you have a certified quality assurance system?
   Yes, we boasts ISO 9001:2015 certified factories.
4. Can I visit your plant before placing an order?
   Of course, we welcome and respect all clients' plant visits.
5. What is the market percentage for domestic and international sales?
   Our domestic market share is approximately 70%, with international sales accounting for less than 30% over the past 5 years.