1.0mm Electric Resistance Wire Bright Surface 0Cr21Al6 0Cr21Al4 0Cr25Al5
FeCrAl Wire 0Cr21Al6 0Cr21Al4 0Cr25Al5 Bare Wire 1.0mm With Bright Surface Used For Heating Furnace
1. Description
FECRAL Has been used extensively as heating elements in industrial furnaces and electrical kilns.
FECRAL Has less hot strength than Tophet alloys but much higher melting point.
Shanghai TANKII ALLOY MATERIAL Co., Ltd.
FECRAL AND ALCHROME ALLOY PRODUCER IN China, MOST PROFESSIONAL IN THE WORLD
We also produce below grades:
Alkrothal 14, Alloy 750, Alferon 902, Alchrome 750, Resistohm 125, Aluchrom, 750 Alloy, Stablohm 750
TANKII A1, TANKII, Alloy 875, Resistohm 145, Aluchrom 0, Alchrome 875, MWS-875, Stablohm 875, KAF TANKII AF, Resistohm Y, Aluchrom Y, Alloy 837, AF KAPM KAPM, Alloy 875 PM, TANKII APM
TANKII D, TANKII, Alloy 815, Alchrome DK, Alferon 901, Resistohm 135, Aluchrom S, Stablohm 812
2.Specification
1).Locomotive resistance strip:
Thickness:0.6mm-1.5mm
Width:60mm-90mm
2).Electric ceramic cooktop resistance strip:
Thickness:0.04mm-1.0mm
Width:5mm-12mm
Thickness&Width:(0.04mm-1.0mm)×12mm(above)
3).Low resistance ribbon:
Thickness&Width:(0.2mm-1.5mm)*5mm
4).Industrial furnace ribbon:
Thickness:1.5mm-3.0mm
Width:10mm-30mm
5).Wire: Diameter:0.1mm-8mm
3. Details of tankii products
| Chemical Composition and Main Property of Fe-Cr-Al Resistance Alloy |
||||||||
| Properties Grade |
1Cr13Al4 |
0Cr25Al5 |
0Cr21Al6 |
0Cr23Al5 |
0Cr21Al4 |
0Cr21Al6Nb |
0Cr27Al7Mo2 |
|
| Main Chemical Composition (%) |
Cr |
12.0-15.0 |
23.0-26.0 |
19.0-22.0 |
22.5-24.5 |
18.0-21.0 |
21.0-23.0 |
26.5-27.8 |
| Al |
4.0-6.0 |
4.5-6.5 |
5.0-7.0 |
4.2-5.0 |
3.0-4.2 |
5.0-7.0 |
6.0-7.0 |
|
| Re |
opportune |
opportune |
opportune |
opportune |
opportune |
opportune |
opportune |
|
| Fe |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
|
| Nb0.5 |
Mo1.8-2.2 |
|||||||
| Max Continuous Service Temperature(oC) |
950 |
1250 |
1250 |
1250 |
1100 |
1350 |
1400 |
|
| Resisivity 20oC (Ωmm2/m) |
1.25 ±0.08 |
1.42 ±0.06 |
1.42 ±0.07 |
1.35 ±0.07 |
1.23 ±0.07 |
1.45 ±0.07 |
1.53 ±0.07 |
|
| Density(g/cm3) |
7.4 |
7.1 |
7.16 |
7.25 |
7.35 |
7.1 |
7.1 |
|
| Thermal Conductivity |
52.7 |
46.1 |
63.2 |
60.2 |
46.9 |
46.1 |
45.2 |
|
| (KJ/m@h@oC) |
||||||||
| Coefficient of Thermal Expansion(α×10-6/oC) |
15.4 |
16 |
14.7 |
15 |
13.5 |
16 |
16 |
|
| Approximate Melting Point( oC) |
1450 |
1500 |
1500 |
1500 |
1500 |
1510 |
1520 |
|
| Tensile Strength(N/mm2) |
580-680 |
630-780 |
630-780 |
630-780 |
600-700 |
650-800 |
680-830 |
|
| Elongation(%) |
>16 |
>12 |
>12 |
>12 |
>12 |
>12 |
>10 |
|
| Section Variation |
65-75 |
60-75 |
65-75 |
65-75 |
65-75 |
65-75 |
65-75 |
|
| Shrink Rate (%) |
||||||||
| Repeatedly Bend Frequency(F/R) |
>5 |
>5 |
>5 |
>5 |
>5 |
>5 |
>5 |
|
| Hardness (H.B.) |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
|
| Continuous Service Time |
no |
≥80/1300 |
≥80/1300 |
≥80/1300 |
≥80/1250 |
≥50/1350 |
≥50/1350 |
|
| Micrographic Structure |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
|
| Magnetic Property |
Magnetic |
Magnetic |
Magnetic |
Magnetic |
Magnetic |
Magnetic |
Magnetic | |
Typical application areas of FeCrAl wires
-
Pre-heating of aluminium
-
Homogenising of aluminium
-
Heat treatment in the metallurgical industry
-
Drying of ore concentrates
-
Drying of materials in the wood processing industry
-
Roasting and drying in the food industry
-
Baking in large bakery ovens
-
Drying of chemicals
-
Drying and stoving of paints (stoving furnaces)
Please call me at +86-18017475212 or email to me for more information on FeCrAl products.
Get in Touch