6mm Stable Resistivity Manganin Copper Alloy Straight Bright Rod Non Insulation
6mm Stable Resistivity Manganin Copper Alloy Straight Bright Bar/ Rod
Product Description
Manganin wire widely used for low voltage instrumentation with the highest requirements, the resistors should be carefully stabilised and the application temperature should not exceed +60 °C. Exceeding the maximum working temperature in air may result in a resistance drift generated by oxidizing. Thus, the long-term stability can be affected negatively. As a result, the resistivity as well as the temperature coefficient of the electric resistance may slightly change. It is also used as low cost replacement material for silver solder for hard metal mounting.
Chemical Content, %
| Ni | Mn | Fe | Si | Cu | Other | ROHS Directive | |||
| Cd | Pb | Hg | Cr | ||||||
| 2~5 | 11~13 | <0.5 | micro | Bal | - | ND | ND | ND | ND |
Mechanical Properties
| Max Continuous Service Temp | 0-100ºC |
| Resisivity at 20ºC | 0.44±0.04ohm mm2/m |
| Density | 8.4 g/cm3 |
| Thermal Conductivity | 40 KJ/m·h·ºC |
| Temp Coefficient of Resistance at 20 ºC | 0~40α×10-6/ºC |
| Melting Point | 1450ºC |
| Tensile Strength(Hard) | 585 Mpa(min) |
| Tensile Strength,N/mm2 Annealed,Soft | 390-535 |
| Elongation | 6~15% |
| EMF vs Cu, μV/ºC (0~100ºC) | 2(max) |
| Micrographic Structure | austenite |
| Magnetic Property | non |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |