0Cr27Al7Mo2 FeCrAl Alloy FeCrAl Heating Rod For Thermocouple
Price:
negotiation
MOQ:
20kg
Delivery Time:
5-10 days
Brand:
TANKII
Product Description
FeCrAl( 0Cr27Al7Mo2) resistance alloy
With the characteristics of high resistance, low coefficient of electric resistance, high operating temperature, good corrosion resistance under high temperature, it is widely used in the single crystal furnace, sintering furnace, ceramic calcining furnace and heat treatment furnace.
0Cr27Al7Mo2
Chemical Content(%)
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other | ||
| Max | |||||||||||
| 0.05 | 0.025 | 0.025 | 0.20 | Max 0.40 | 26.5~27.8 | Max 0.60 | 5.0~7.0 | Bal. | Mo 1.8-2.2 | ||
Mechanical Properties
| Max Continuous Service Temp | 1350ºC |
| Resisivity at 20ºC | 1.45 ohm mm2/m |
| Density | 7.1 g/cm3 |
| Thermal Conductivity | 46.1 KJ/m·h·ºC |
| Coefficient of Thermal Expansion | 16.0×10-6/ºC |
| Melting Point | 1510ºC |
| Tensile Strength | 637~784 Mpa |
| Elongation | Min 12% |
| Section Variation Shrink Rate | 65~75% |
| Repeatedly Bend Frequency | Min 5 times |
| Continuous Service Time | - |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |
Temperature Factor of Electrical Resistivity
| 20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 500ºC | 600ºC | 700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1200ºC |
| 1 | 0.997 | 0.996 | 0.994 | 0.991 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Shanghai Tankii Alloy Material Co.,Ltd
Location
1900 Mudanjiang Road, Baoshan District, 201999, Shanghai, China
Contact Person
Martin Lee