Kan-Thal D FeCrAl 135 Electrical High Temperature Heater Wire For Chemical

Price Negotiable

Price: negotiable

MOQ: 100 KG

Delivery Time: 7-20 days

Brand: TANKII

Product Description

FeCrAl alloy has the characteristic of high resistivity, low temperature resistance coefficient, high operating temperature, good anti-oxidation and anti-corrosion under high temperature.

It is widely used in industrial furnace, household appliances, metallurgy, machinery, aircraft, automotive, military and other industries producing heating elements and resistance elements.

Size details

Product name	Size range
Cold drawing wire	Diameter 0.03-7.5mm
Hot-rolled wire rod	Diameter 8.0-12mm
Ribbon	Thickness 0.05-0.35mm
Ribbon	Width 0.5.0-3.5mm
Cold rolled strip	Thickness 0.5-2.5mm
Cold rolled strip	Width 5.0-40mm
hot rolled strip	Thickness 4-6mm
hot rolled strip	Width 15-40mm

basic parameters:

basic parameters	APMTM	FeCrAl
basic parameters	APMTM	A-1	AF	D
The highestcontinuous working temperature	1425	1400	1300	1300
The nominal chemical composition,% Cr	22	22	22	22
AI	5.8	5.8	5.3	4.8
Fe	ingredients	ingredients	ingredients	ingredients
Ni	-	-	-	-
The resistivity in 20ºC,Ωmm-2mm-1	1.45	1.45	1.39	1.35
density,g/cm3	7.1	7.1	7.15	7.25
Thermal expansion coefficientK-1 20-750ºC	14×10-6	14×10-6	14×10-6	14×10-6
20-1000ºC	15×10-6	15×10-6	15×10-6	15×10-6
The thermal conductivity 20ºC,Wm-1K-1	13	13	13	13
Specific heat capacity 20ºC,KJkg-1K-1	0.46	0.46	0.46	0.46
Melting pointºC	1500	1500	1500	1500
Probably mechanical characteristics
Tensile strength,N mm-2	680	680	680	650
The yield strength,N mm-2	470	475	475	450
Hardness,Hv	230	230	230	230
Breaking elongation,%	20	18	18	18
900ºCTensile strength,N mm-2	40	34	37	34
Creep strength 800ºC	11	6	8	6
1000ºC	3.4	1	1.5	1
Magnetic	magnetic(In the temperature600ºC)
Emissivity, the oxidation conditions	0.7	0.7	0.7	0.7