60Si2MnA Fastening Systems Rail E Type Clip，rail elastic clip
60Si2MnA Fastening Systems Rail E Type Clip
E Clamp Rail Fastening System
Technical Parameters
|
Part name |
Type |
Material |
Finish |
Remark |
|
|
E clip |
Dia. 16mmDia. 18mmDia. 20mm |
60Si2MnA, 60Si2CrA 55SiMn |
Plain oiled, color painting, or the other custom finish |
Hardness: 44-48HRC |
|
|
Shoulder |
UIC54,UIC60, 115RE,50kg rail, 60kg rail, BS80lbs,BS100lbs |
QT500-7 QT450-10 |
Plain oiled, color painting |
Different designs are available. |
|
|
Rail pad |
UIC54,UIC60, BS80lbs,BS100lbs, in ordered size |
HDPE EVA rubber |
Black or other colors |
Different designs are available. |
|
|
Insulator |
UIC54,UIC60, 50kg rail, 60kg rail,BS80lbs,BS100lbs, and size as ordered |
Reinforced Nylon 66 (PA66) |
Black, blue, yellow, green or other colors |
Different designs are available. |
|
Breakdown Drawing
Material
| Material | ||||
| Grade | 4.6 | 5.6 | 8.8 | 10.9 |
| Material | Q235 | 35# | 45# | 40Cr |
| Mechanical properties | Tensile strength: ≥400Mpa | Tensile strength:≥500Mpa | Tensile strength:≥800Mpa | Tensile strength:≥1000Mpa |
| Yield strength:≥240Mpa | Yield strength:≥300Mpa | Yield strength:≥640Mpa | Yield strength:≥900Mpa | |
| Elongation:≥22% | Elongation:≥20% | Elongation:≥12% | Elongation:≥9% | |
| Cold bending: 90 degree without crack | ||||
| Surface | plain (oiled), Oxide black, Zinc, HDG, wax, bitumen, Dacromet, Sherardizing | |||
Note ( 8.8 as a sample)
the first 8: tensile strength of material 45# is 800MPa;
the second 0.8: the yield ratio is 0.8;
the yield strength of material 45# is 800MPa x 0.8 = 640 MPa.
Clip Material
- 60Si2MnA
- 60Si2CrA
- 55Si2Mn
- 38Si7
Process
- Clip as a sample
- raw material
- shearing
- heating to forging temperature (950-1000 degrees celsius)
- forming
- hardening
- tempering below 350 degrees celsius
- inspection
- packing
Surface Treatment
- plain (oiled)
- color paint
- oxide Black (most choice)
- galavazing
- DHG
Inspection machine
- Brinell Hardness Tester
- Carbon and Sulfur Analyzer
- Rockwell Hardness Machine
- Automatic Impact Testing Machine
- Metallographic Microscope
- Automatic High-speed Analyzer
- Fatigue Testing Machine
- Metallographic Specimen Polishing Machine
- Metallographic Specimen Pointing Machine
Package
1. 25kg per double layer woven bag+ free fumigation wooden pallet
36bags/pallet,
24pallets/container
2. Keg
3. in according with your request
Application
Similarity
- E CLIP SYSTEM
- NABLA SYSTEM
- SKL 1 / 2 / 3 / 12 / 14 CLIP SYSTEM
- FIST CLIP SYSTEM
- SPECIAL CLAMP SYSTEM
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.