High Strength Durable Light 3K Carbon Fiber Board Composite Sheet 500mmx500mm

Carbon fiber composite sheets are flat, rigid structures made from layers of carbon fiber fabric bonded together with a resin. These sheets are known for their high strength-to-weight ratio, stiffness, and corrosion resistance, making them ideal for a variety of applications.

The carbon plates are manufactured using the thermal high-pressure hot-press process and therefore have a high fiber volume content of >65%. An epoxy resin matrix serves as the matrix material. The carbon plates are made of carbon fabric throughout and have a homogeneous, biaxial fiber distribution in 0°/90°.

The outer layers are made of 3K fabric in a twill weave, are smooth and have the typical visible carbon fabric structure.

Due to the high pressing pressure during the manufacturing process, these carbon plates achieve outstanding properties in the area of ​​flexural strength as well as torsional and dimensional stability.

The panels have the following characteristic laminate values:

Flexural strength EN2562: 850 MPa
Flexural modulus EN2562: 60 GPa
Tensile strength ISO 527: 650 MPa
Tensile modulus of elasticity ISO 527: 60 GPa
Coefficient of thermal expansion: 1 E^-06 1/K
I.L.S.S. EN2563: ~70MPa
Density: 1.56 g/cm³
Fiber weight percentage: >65%
Glass transition temperature (short term): 130°C (180°C)
Water absorption: < 0.04%

Single-Sided Carbon Fiber Plate Specification: