Pultruded Carbon Fiber Pipe , Filament Wound Fiberglass Tube Good Tenacity

Pultruded Carbon Fiber Pipe , Filament Wound Fiberglass Tube Good Tenacity

Carbon Fiber Pipe Features

Light Weight - Less Density

High Strength

Good Tenacity and dimensional Stability

High corrosion resistance
Nice appearance

Factory directly sale

Carbon Fiber Pipe Specification          

Carbon fiber winding of molding process

Winding molding process is soaked in resin adhesive solution of continuous fiber (or cloth belt, presoak

yarn) on winding to the mandrel according to certain rules, and then after curing, demoulding, obtain 

products.According to the filament winding forming physical and chemical condition when the resin is 

different, divided into dry winding, wet winding and half dry winding 3 kinds.(1) dry winding Dry winding

is adopted through presoak rubber processing presoak yarn or, on a winding machine after soften to 

viscous flow winding onto the mandrel.Because of presoak yarn (or with) is a professional production, to

strictly control the resin content (accurate to 2%) and presoak yarn quality.Therefore, dry winding can

accurately control the quality of the product.Dry winding process is the biggest characteristic of high 

production efficiency, winding speed can reach 100 ~ 100 m/min, winding machine cleaning, labor health 

condition is good, high product quality.The downside is winding equipment is expensive, need to increase

in yarn manufacturing equipment, so the investment is bigger also, dry low interlaminar shear strength 

of winding products.

(2) the wet winding Wet winding is fiber cluster (yarn belt), glue, directly under tension control winding 

onto the mandrel.The advantages of wet winding for: (1) 40% lower cost than dry winding;(2) the product 

has good air tightness, because of the winding tension to squeeze bubbles, the excess resin adhesive

liquid and fill gaps;(3) fiber arrangement good parallelism;(4) the wet winding, fiber resin adhesive 

solution, can reduce the fiber abrasion;5. High efficiency (up to 200 m/min).Wet winding faults as follows:

(1) resin waste is big, poor operating environment;(2) gel content and quality of the finished product is

not easy to control;(3) less available for wet winding resin varieties.