Alumina Silicon Carbide ballistic tile Boron carbide Ceramic Tile Typical for Bullet Proof Plate
Alumina Silicon Carbide ballistic tile / Boron carbide Ceramic Tile Typical for Bullet Proof Plate
Specifications
• made of boron carbide ,silicon carbide or Alumina
• lightweight,high toughness
• for aircraft armor,vehicle armor
• for body armor
Description:
Boron carbide bulletproof armor plate is made by sintereting boron carbide abrasive grain in the
high pressure vacuum sintering furnace, from room temperature to a certain temperature, keep this temperature for several hours then naturally cooling to room temperature again, then processing it mechanically to reach a required tolerance.
Applications:
Ceramic bulletproof armor plate is suitable for making lightweight bulletproof armor, using to protect aircraft, vehicle, naval vessel and making bullet-proof vest.
Typical Chemical Analysis:
Total Boron 77.90%
Total Carbon 20.98%
Fe2O3 0.16%
B+C 98.88%
B4C 95.85%
Physical Properties:
Color Grey
Bending Strength 469Mpa
Fracture Toughness 4.2Mpa.m1/2
Density 2.56 g/cm3
Hardness 30.83Gpa, Vickers
Dimension Available :
|
Length(mm) |
Width(mm) |
Thickness(mm) |
|
50 |
50 |
8-10 |
|
150 |
150 |
5-10 |
|
200 |
200 |
5-10 |
Hexagon, single spherical side, double spherical side, arc shape and OEM dimension available upon request.
Material Comparation Chart:
|
Item |
Al2O3 |
SiC |
B4C |
|
Density |
3.5g/cm3 |
3.1g/cm3 |
2.4-2.65g/cm3 |
|
Hardness |
HV1650 |
HV2750 |
HV3300 |
|
Flexural strength |
290 Mpa |
380 Mpa |
400-650 Mpa |
|
Compressive strength |
850 Mpa |
3970 Mpa |
4100 Mpa |
|
Fracture toughness |
4.8 Mpa.m1/2 |
4.0 Mpa.m1/2 |
4.5-7.0 Mpa.m1/2 |
|
Thermal Conductivity |
20 m0k |
120m0k |
29 m0k |
Workshop & Warehouse & Lab: