90 Shore ST2 Injection Grade PVC Cable Granules Material factory
High Quality 90 Shore ST2 Injection grade PVC Cable granules for Wire and Cable
Product Introduction:
The stabilizer of environmental protection cable material is generally calcium-zinc stabilizer.
It is important that the PVC cable material that meets the REACH standard cannot use 16 kinds of substances such as DEHP as plasticizers.
Non-environmental cable materials generally use lead salts as stabilizers. Because they contain heavy metals such as lead, chromium, cadmium, mercury, barium and other heavy metals, they will cause great damage to the environment and human health, and are subject to more and more national restrictions or Prohibited to use.
The insulation and sheath of wires and cables used in low voltage (below 1 k V) lines and electrical equipment can be covered with PVC, while the sheaths of medium and high voltage (greater than 6 k V) wires and cables are mostly PVC Cladding.
PVC Compound for Generic Cable
Good processing technology, suitable to various cables.
Product Name:
- 70 ℃ PVC Cable Compound
- 90 ℃ PVC Cable Compound
- 105 ℃ PVC Cable Compound
- 105 ℃ Irradiated crosslinked FR PVC Compound
- 80 ℃ Irradiated crosslinked FR PVC Compound
- PVC Compound for Plug
The standard finish of all cables consists of an extruded black PVC oversheath, the external surface of which is embossed with the appropriate legend.
The oversheath PVC grade is usually Type TM 1 or Type 9 to BS 7655 although other grades, e.g., Type 5 (85°C Hard) PVC or PVC sheath with anti-termite properties can be provided when specified. The PVC grade is ST2 for cables conforming to IEC 60502- 1 standard.
Technical Data:
| Items | Unit | Typical Value | Testing Method | ||
| 70 ℃ PVC Cable Compound | 105 ℃ PVC Cable Compound | 105 ℃ Irradiated crosslinked FR PVC Compound | |||
| Tensile Strength | Mpa | 11 | 11 | 12 | GB/T 1040.3-2006 |
| Elongation at Break | % | 180 | 180 | 180 | |
| Heat Aging | |||||
| Testing Termperature | ℃ | 100 | 135 | 135 | GB/T 8815-2008 |
| Testing Time | h | 168 | 168 | 168 | |
| Variation at tensile strength | % | 20 | 20 | 20 | |
| Variation at elongation | % | -15 | -15 | -15 | |
| Low Temperature Brittleness | ℃ | -20 | -20 | -20 | GB/T 5470-2008 |
| Oxygen Index | / | ≥23 | ≥23 | ≥28 | GB/T 2406.2-2008 |
| Density | g/cm3 | 1.42 | 1.42 | 1.42 | GB/T 1033.1-2008 |
| Hardness | Shore A | 70-96 | 70-96 | 70-96 | GB/T 2411-2008 |
Product Show:
Storage :These compounds must be stored at ambient temperature (not exceeding 30’C) in closed and unbroken packaging ,in order to avoid exposure to sunlight and water absorption.
Packaging : Available in 25Kg plastic bags, big bags, carton oktabins or in slos truck