Shock Proof 90 Shore PVC Granules For Communication Cable Insulation
Shock Proof REACH Compliant 90 Shore Cable Grade PVC Granules Insulating Compound For Communication Cables
Wire and Cable Insulation and Jacket PVC Compounds
Product Introduction:
flame-retardant PVC designed for applications that need to pass UL 1581, UL 1685, UL 1666 (datacom, coaxial, control, signal, energy, building wire)
PVC cable compounds are used extensively to protect and insulate cables in a variety of applications due to the benefits that PVC cable compounds offer such as cost effectiveness, flame retardancy and durability. Additives can also be added to a base PVC cable compound to support additional stamina against environmental factors if the application requires it.
Product Name:
- 70 ℃ PVC Cable Compound
- 90 ℃ PVC Cable Compound
- 105 ℃ PVC Cable Compound
- 105 ℃ Irradiated crosslinked FR PVC Compound
- 80 ℃ Irradiated crosslinked FR PVC Compound
- PVC Compound for Plug
Soft PVC cable insulation compounds
Depending on requirements, cable insulation mass compunding systems utilizes various different plastics. They include polyolefin, TPE, PPE, EEFE, PVA, and of course soft PVC compounds. PVC has been used for cable insulation since 1932, originally as a replacement for rubber. Due to their relatively high dielectric strength, leading to corresponding induction losses and heating, soft PVC cable insulation compounds are only used at AC voltages of up to 10 kV. Most soft PVC cable mass applications are in this field. Formulations can be adjusted to customize the application temperature range, mechanical characteristics and flexibility of use, flammability and processing.
Technical Data:
| Items | Unit | Typical Value | Testing Method | ||
| 70 ℃ PVC Cable Compound | 105 ℃ PVC Cable Compound | 105 ℃ Irradiated crosslinked FR PVC Compound | |||
| Tensile Strength | Mpa | 11 | 11 | 12 | GB/T 1040.3-2006 |
| Elongation at Break | % | 180 | 180 | 180 | |
| Heat Aging | |||||
| Testing Termperature | ℃ | 100 | 135 | 135 | GB/T 8815-2008 |
| Testing Time | h | 168 | 168 | 168 | |
| Variation at tensile strength | % | 20 | 20 | 20 | |
| Variation at elongation | % | -15 | -15 | -15 | |
| Low Temperature Brittleness | ℃ | -20 | -20 | -20 | GB/T 5470-2008 |
| Oxygen Index | / | ≥23 | ≥23 | ≥28 | GB/T 2406.2-2008 |
| Density | g/cm3 | 1.42 | 1.42 | 1.42 | GB/T 1033.1-2008 |
| Hardness | Shore A | 70-96 | 70-96 | 70-96 | GB/T 2411-2008 |
Product Show:
Storage :These compounds must be stored at ambient temperature (not exceeding 30’C) in closed and unbroken packaging ,in order to avoid exposure to sunlight and water absorption.
Packaging : Available in 25Kg plastic bags, big bags, carton oktabins or in slos truck
A team of highly proficient and dedicated engineers, scientists and technical staff continuously works in order to respond to the challenges of the times effectively.
Providing wide range of Soft and Rigid PVC Compound for various applications, According to BS, IEC, UL, ASTM, VDE, DIN complying with RoHS and REACH requirements
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.