Electronic Polyvinyl Chloride Pellets Cable Wire Insulation Compound 1.5G/CM3
Fire Retardant PVC Pellets Cable Wire Insulation Compound Density 1.5G/CM3
Product Introduction:
PVC based plasticizers have considerable mechanical strength and water resistance, high thermal resistance to low temperatures, good insulation properties, insoluble in gasoline and kerosene, abrasion, acid and alkali resistant. PVC based compounds are readily welded and glued.
Cable PVC compounds are use in the cable and conductor industry for manufacture of insulation and protective wire and cable sheaths. The main final consumers of the PVC based cable and conductor products are energy and construction industries.
Product Name:
- 70 ℃ PVC Cable Compound
- 90 ℃ PVC Cable Compound
- 105 ℃ PVC Cable Compound
- 105 ℃ Irradiated crosslinked FR PVC Compound
- 80 ℃ Irradiated crosslinked FR PVC Compound
- PVC Compound for Plug
Technical Data:
| Items | Unit | Typical Value | Testing Method | ||
| 70 ℃ PVC Cable Compound | 105 ℃ PVC Cable Compound | 105 ℃ Irradiated crosslinked FR PVC Compound | |||
| Tensile Strength | Mpa | 11 | 11 | 12 | GB/T 1040.3-2006 |
| Elongation at Break | % | 180 | 180 | 180 | |
| Heat Aging | |||||
| Testing Termperature | ℃ | 100 | 135 | 135 | GB/T 8815-2008 |
| Testing Time | h | 168 | 168 | 168 | |
| Variation at tensile strength | % | 20 | 20 | 20 | |
| Variation at elongation | % | -15 | -15 | -15 | |
| Low Temperature Brittleness | ℃ | -20 | -20 | -20 | GB/T 5470-2008 |
| Oxygen Index | / | ≥23 | ≥23 | ≥28 | GB/T 2406.2-2008 |
| Density | g/cm3 | 1.42 | 1.42 | 1.42 | GB/T 1033.1-2008 |
| Hardness | Shore A | 70-96 | 70-96 | 70-96 | GB/T 2411-2008 |
Product Show:
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.