Oxidation Heat Resistant Coatings Alloy 625 Wire Hrb 92 Typical Hardness
Oxidation Heat Resistant Coatings Alloy 625 Wire Hrb 92 Typical Hardness
RODUCT OVERVIEW
Alloy 625 is a high purity nickel chrome wire specifically designed for arc spraying. It produces dense, well-bonded coatings with resistance to corrosion, and stress cracking in caustic mediums.
TYPICAL DEPOSIT CHARACTERISTICS:
Þ Typical Hardness: HRB 92
Þ Bond Strength: 7000 psi
Þ Deposit Rate: 11 lbs/hr/100A
Þ Deposit Efficiency 70%
Þ Wire Coverage: 0.8 oz/ft2 / mil
Þ Surface Texture * Variable
* Depends on air pressure used
SURFACE PREPARATION
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning.
Recommended method of preparation is to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
APPLICATION
Þ Oxidation and heat resistant coatings
Þ Corrosion resistance
Þ Digesters
SPECIFICATION
Alloy 625
NOMINAL CHEMICAL COMPOSITION (wt%)
| Ni | Cr | Mo | Fe | Cb+Ta |
| 62.5 | 22 | 10.0 | 2.0 | 3.5 |
RECOMMENDED SPRAY PARAMETERS:
| Diameter | Air Pressure | Voltage | Amperage | Standoff |
| 1/16” (1.6mm) | *50-60 psi | *29-32 | *50-300 | *4-8 in (10-20 cm) |
* Parameters are typical and may vary depending on equipment used. Contact your equipment manufacturer for optimum spray parameters
STANDARD SIZES & PACKAGING:
| Diameter | Packaging |
| 1/16” (1.6mm) | 15kg/spool |