Double row ball slewing bearing with teeth 4548.6x3970x187mm for heavy duty industry machine

 Double row four point contact ball slewing bearing with teeth 4548.6x3970x187mm for heavy duty industry machine

The slewing bearing with teeth 4548.6x3970x187mm belongs to over size bearing,It has two row raceway to running,The bearing can support high static loads with simple structure. They are mainly used in situations with variational load position and direction and continuously rotating. Main applications of this kind of bearings are desk hoisting,mining and material handling.

The slewing bearing 4548.6x3970x187mm technology data as following:

For the slewing bearing, Please reference actual pictures:

Forging process:
The blanks of bearing rings are mainly made of rods and tubes, while the forging process is only applicable to rods. However, forgings are the most used blank materials in bearing manufacturing, and are suitable for large and medium-sized bearings. Forging can be divided into hot forging, cold forging and warm forging. Hot forging refers to processing above the re-crystallization temperature of the billet metal, warm forging is forging at a temperature not exceeding the re-crystallization temperature, and cold forging refers to forging at normal temperature.

The purpose of ferrule forging: 1. Through forging, obtain a blank with a size similar to the product, improve the utilization of metal materials, reduce the amount of machining, and reduce costs. 2. Forging can eliminate the internal defects of the metal, improve the structure, and thus increase the service life of the bearing.
General process of forging:
Bar material ,inspection, heating, blanking, secondary heating, forging, rolling,cooling, annealing, cleaning

Rough turning: Rough turning is performed according to the drawing of the turning process, and the cutting speed and cutting amount are strictly implemented according to the technical regulations (the general cutting speed is 5 rpm. The cutting amount is 10mm ~ 12mm).
2.2 Rough turning aging: After the rough turning of bearing parts is completed, three-point support and flat laying is not allowed (stacking is not allowed), and the precision turning processing can be performed after the aging time is not less than 48 hours.
2.3 Fine turning bearing parts When finishing turning, the cutting speed is 6 to 8 revolutions per minute, and the cutting amount is 0.3 to 0.5 mm.
2.4 Precision turning: In order to prevent the parts from deforming when the bearing parts are finally finished, the parts must be loosened to make the parts in a non-stressed state. The turning speed is 8 revolutions per minute and the cutting amount is 0.2 mm.
2.5 Cross and three-row roller slewing bearing inner ring special process: To prevent cross and three-row roller slewing bearing inner ring from deforming after heat treatment. The turning process must be performed in pairs, that is, the raceway is back-to-back processing. No cutting is performed before heat treatment, and cutting is performed after heating.
2.6 Finished car after heating: After the inner and outer rings of the bearing are heat-treated, the finished car turning process is carried out, and the technical procedures are the same as 2.3 and 2.43)

Slewing bearings perform extremely well in a variety of applications such as:
• access platforms
• bucket wheel excavators
• conveyor booms
• cranes of all types
• small, medium and large excavators
• indexing table
• ladle turrets
• offshore applications
• robots
• railway bogies
• rotary platforms
• stackers
• solar mirrors
• tunnel boring machines
• wind turbines