high density isostatic graphite rod

Price Negotiable

Price: USD1000/MT

MOQ: 25

Delivery Time: 10-15days

Brand: Haisen

Product Description

high density isostatic graphite rod

Application:

1,electordes and graphite anodes

2,main graphite materials to machine graphite products

3, indiustry furnaces used graphite products

4,heating rods and graphite molds

5,graphite stopper and grounded graphite products

Price:

Price of such graphite products is according to customers' design or sizes details, so pls email us,

we will have a accurate price for you.

Grade	Item	Unit	Reference Data	Main Application
DJY-I	Average grain size	mm	≤0.025	Mainly used to machine graphite parts with very high reuqirement. 1-used in electronic,photovoltaic industries, such as precision circuit board, core parts of thermal field. 2-used in precision casting industries, such as copper continuous casting parts. 3-used in precision machining, such as EDM graphite. 4-used to machine graphite crcuible for melting rare metals. 5-used to machine analysis container in labs, such as graphite boat/dish, graphite container 6-used in hard alloy industry, such as sintering molds.
	Bulk density	g/cm3	≥1.70
	Specific Resistivity	µΩm	≤15.0
	Flexural Strength	Mpa	≥28.0
	Compressive Strength	Mpa	≥56.0
	Shore Hardness	HS	≥50.0
	Elastic Modulus	GPa	≤9.5
	C.E.T(100-600°C)	-10-6/°C	≤3.2
	Ash	%	≤0.07
DJY-II	Average grain size	mm	≤0.025
	Bulk density	g/cm3	≥1.75
	Specific Resistivity	µΩm	≤15.0
	Flexural Strength	Mpa	≥35.0
	Compressive Strength	Mpa	≥70.0
	Shore Hardness	HS	≥55.0
	Elastic Modulus	GPa	≤10.0
	C.E.T(100-600°C)	-10-6/°C	≤3.8
	Ash	%	≤0.07
DJY-Ⅲ	Average grain size	mm	≤0.025
	Bulk density	g/cm3	≥1.80
	Specific Resistivity	µΩm	≤14.0
	Flexural Strength	Mpa	≥37.0
	Compressive Strength	Mpa	≥75.0
	Shore Hardness	HS	≥55.0
	Elastic Modulus	GPa	≤10.5
	C.E.T(100-600°C)	-10-6/°C	≤4.2
	Ash	%	≤0.07
DJY-IV	Average grain size	mm	≤0.025
	Bulk density	g/cm3	≥1.85
	Specific Resistivity	µΩm	≤13.0
	Flexural Strength	Mpa	≥42.0
	Compressive Strength	Mpa	≥85.0
	Shore Hardness	HS	≥55.0
	Elastic Modulus	GPa	≤11.0
	C.E.T(100-600°C)	-10-6/°C	≤4.5
	Ash	%	≤0.07