AISI 310S Stainless Steel Strip Roll NO1 Finish Hot Rolling Seaworthy Package
ASTM AISI 310S 321 316 BA 2B Cold Rolling Stainless Steel Strip Coil Customized
1. Products Details
AISI 310s
UNS S31008
EN 1.4845
Grade 310S is used when the application environment involves moist corrodents in a temperature range lower than that which is normally considered "high temperature" service. The lower carbon content of 310S does reduce its high temperature strength compared to 310.
| Grade | 310S stainless steel strip |
| Thinckness | 0.3-6.0mm |
| Tolerance | +/-0.02mm |
| Widthness | 6mm-600mm |
| Length | as coils |
| Brand name | TISCO,L;ISCO,BAOSTEEL |
| Standard | JIS, AISI, ASTM, GB, DIN, EN ,etc. |
| Finish | 2B, NO1,Hairline, No.4, BA, 8K mirror, etc. |
| Certification | SGS |
| Packaging | Standard exporting packing; seaworthy package. |
| MOQ | 1 Tons |
| Price time | FOB, CFR, CIF, CNF |
| Delivery time | Within 15-20 working days after receiving your deposit |
| Payment | 30% T/T in advanced+70% balanced; irrevocable L/C at sight |
| Remarks | Insurance is all risks and accept the third party test |
2. Chemical Properties: 310S 310
| 310S | C | Si | Mn | P | S | Ni | Cr |
| ≤0.08 | ≤1.50 | ≤2.00 | ≤0.045 | ≤0.03 | 19.00~22.00 | 24.00~26.00 |
Mechanical Properties:
| Grade | Tensile Strength ksi (min.) |
Yield Strength 0.2% Offset ksi (min.) |
Elongation - % in 50 mm (min.) |
Hardness (Brinell) MAX |
Hardness (Rockwell B) MAX |
|---|---|---|---|---|---|
| 310/310S | 75 | 30 | 40 | 217 | 95 |
Physical Properties:
| Denstiy lbm/in3 |
Coefficient of Thermal Expansion (min/in)-°F |
Electrical Resistivity mW-in | Thermal Conductivity BTU/hr-ft-°F | Specific Heat BTU/lbm -°F | Magnetic Permability (annealed)1 | Modules of Elasticity (annealed)2-psi | |||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| at 68 °F | at 68 – 212°F | at 68 – 932°F | at 68 – 1832°F | at 68°F | at 1200°F | at 68 – 1832°F | at 68 – 932°F | at 32 – 212°F | at 200H | in tension (E) | in shear (G) |
| 0.29 | 8.8 | 9.5 | 10.5 | 30.7 | — | 10.5 | 10.8 | 0.12 | 1.02 | 29 x 106 | 11.2 x 106 |
2. Applications
The higher alloyed stainless steels generally have excellent strength at elevated temperatures along with outstanding resistance to creep deformation and environmental attack. Therefore, Alloy 310 is used widely in industries such as heat treatment and chemical processing. Some examples include:
Furnace Parts
Oil Burner Parts
Heat Exchangers
Welding Filler Wire and Electrodes
Annealing Covers
Combustion Tubes
Fire Box Sheets
3. Hot Rolling Production Line For 321 SS Coil Processsing
|
Thickness (mm) |
Witth (mm) |
Length (mm) |
Precision (mm) |
Straightness (mm) |
Length Error (mm) |
Trimedge Thickness (mm) |
| 3.0-8.0 | 800-1600 | 1000-150000 | ≤±1.5 | ≤±1.0 | ≤±1.5 | ≤8.0 |
| 6.0-14.0 | 1000-2000 | ≤14.0 | ||||
| 8.0-18.0 | 1250-2000 | ≤16.0 |