95%-99.98% AZ80A Extruded Magnesium Alloy Bar Rod Billet for Electronics , Machinery Parts
95%-99.98% AZ80A Extruded Magnesium Alloy Bar Rod Billet for Electronics , Machinery Parts
Details:
Name: magnesium alloy bar,dissolvable magnesium bar.
Specification: Ø50mm,Ø60mm,Ø70mm,Ø80mm,Ø90mm,Ø100mm…..Or customized according to customer requirements.
AZ80A magnesium alloy is an alloy composed of magnesium and other elements added as the base. Its characteristics are: low density (about 1.8g/cm3 magnesium alloy), high specific strength, large specific modulus of elasticity, good heat dissipation, good shock absorption, greater impact load capacity than aluminum alloy, resistance to organics and alkali corrosion it is good. The main alloying elements of AZ80A are aluminum, zinc, manganese, cerium, thorium and a small amount of zirconium or cadmium.
| Hilbo magnesium alloy material Co., Ltd. | ||||||||||||||
| Quality Inspection Report | ||||||||||||||
| NO:JB/MS03-151-1236 | ||||||||||||||
| Model | Specifications | Process | Furnace No. | Chemical Composition (%) | Low power test | |||||||||
| Al | Zn | Mn | Fe | Si | Cu | Ni | Mg | Low power | Surface quality | Size | ||||
| Ø80*1000 | Extrussion | 9850 | 8.5 | 0.60 | 0.3 | 0.005 | 0.1 | 0.05 | 0.005 | Balance | OK | OK | OK | |
| AZ80A H112 |
||||||||||||||
| Magnesium alloy bar | ||||||||||||||
| Tensile strength Rm /Mpa |
Yield strength 0.2% Mpa |
Elongation at break % | ||||||||||||
| 295 | 190 | 5 | ||||||||||||
| Conclusion :Passed inspection | ||||||||||||||
Magnesium Alloy Chemical Composition:
|
Model
|
chemical component(%) |
||||||
|
Type |
Mg |
Al |
Zn |
Mn |
Si |
Fe |
Cu |
|
AX31B |
residual |
2.5-3.5 |
0.60-1.4 |
0.20-1.0 |
≤0.08 |
≤0.003 |
≤0.001 |
|
AZ61A |
|
5.8-7.2 |
0.40-1.5 |
0.15-0.50 |
≤0.10 |
≤0.005 |
≤0.005 |
|
AZ80A |
|
7.8-9.2 |
0.20-0.80 |
0.12-0.50 |
≤0.10 |
≤0.005 |
≤0.005 |
|
AZ91D |
|
8.5-9.5 |
0.45-0.90 |
0.17-0.40 |
≤0.08 |
≤0.004 |
≤0.001 |
Product Advantages:
- Dissolves even at minimal electrolyte concentrations (from 1%) and any temperature.
- The degradation by-product is a fine powder that does not interfere with production.
- Any size available.
Performance test data:
| No. | Model | Test condition | Dissolution rate mg/(cm2*h)) |
Strength of extension(MPa) | Yield strength(MPa) | Elongation (%) |
Hardness (HB) |
| 1 | HB006 | 93℃/3%KCl | 50-70 | ≥370 | ≥260 | ≥2.5 | ≥90 |
| 2 | HB006A | 93℃/3%KCl | 50-70 | ≥310 | ≥220 | ≥6.0 | ≥75 |
| 3 | HB008 | 93℃/3%KCl | 40-60 | ≥400 | ≥300 | ≥4.0 | ≥100 |
| 4 | HB008B | 93℃/3%KCl | 40-60 | ≥370 | ≥270 | ≥5 | ≥100 |
| 5 | HB008C | 93℃/3%KCl | 40-60 | ≥310 | ≥220 | ≥15 | ≥85 |
| 6 | HB012 | 93℃/3%KCl | 40-60 | ≥400 | ≥300 | ≥3.0 | ≥100 |
| 7 | HB011 | 93℃/3%KCl | 15-35 | ≥420 | ≥300 | ≥3.0 | ≥100 |
| 8 | HB016 | 93℃/3%KCl | 35-55 | ≥280 | ≥180 | ≥15 | ≥60 |
| 9 | HB017 | 93℃/3%KCl | 40-50 | ≥200 | ≥140 | ≥17 | ≥55 |
| 10 | HB018K | 50℃/0.84KCl | 50-70 | ≥240 | ≥170 | ≥12 | ≥55 |
| 11 | HB018 | 50℃/0.84KCl | 30-50 | ≥230 | ≥170 | ≥12 | ≥55 |
| 12 | HB010 | 93℃/3%KCl | 15-35 | ≥190 | ≥120 | ≥30 | ≥45 |
| 13 | HB022 | 43℃/0.05%KCl | 50-60 | ≥300 | ≥200 | ≥5.0 | ≥75 |
| 14 | HB023 | 43℃/0.05%KCl | 20-40 | ≥280 | ≥200 | ≥7.5 | ≥65 |
| 15 | HB024 | 43℃/0.05%KCl | 50-70 | ≥260 | ≥220 | ≥5 | ≥60 |
| 16 | HB013A | 43℃/0.05%KCl | 80-100 | ≥260 | ≥230 | ≥3.5 | ≥75 |
| 17 | HB025 | 50℃/0.84%KCl | 90-110 | ≥275 | ≥200 | ≥12 | ≥65 |
| 18 | HB026 | 93℃/3%KCl | 20-40 | ≥450 | ≥350 | ≥3.0 | ≥110 |
| 19 | HB808 | 50℃/0.84%KCl | 50-70 | ≥370 | ≥260 | ≥3.0 | ≥100 |
| 20 | HB019 | 50℃/0.84KCl | 45-65 | ≥230 | ≥180 | ≥12.0 | ≥55 |
| 21 | HB055 | 93℃/3%KCl | 130-150 | ≥220 | ≥160 | ≥12.0 | ≥55 |
| 22 | HB035 | 93℃/3%KCl | 50-100 | ≥100 | ≥60 | ≥42.0 | ≥35 |
| 23 | HBMM6 | 50℃/0.84%KCl | 70-100 | ≥260 | ≥230 | ≥10.0 | ≥60 |
| 24 | HBMM7 | 50℃/0.84%KCl | 90-120 | ≥270 | ≥240 | ≥9.0 | ≥65 |
| 25 | HBMM8 | 93℃/3%KCl | 100-150 | ≥280 | ≥250 | ≥5.0 | ≥65 |
Advantage of Hilbo Company:
Full range of product types, Ensure production capacity
We ave advanced die-casting, extrusion, forging, rolling, casting processing production line and precision testing equipment. Can produce a variety of types of magnesium alloy and magnesium alloy products, and developed a high-strength magnesium alloy extruded sheet. Through the purification of ordinary magnesium, magnesium can be raised up to 99.99% of high purity.
Cost advantage
Magnesium alloy casting production can customized as your requirement. the technical process is great, extrusion production required for a variety of bar, no need to purchase from abroad, extrusion molding products is easy molding, low energy consumption, saving production costs.
Workshop:
Testing Equipment
Certificate:
We have attained ISO9001 and ISO14001 certificates, Standardize and improve the enterprise quality management system.
FAQ:
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.