High Temperature Resistance Ceramic Oxide Disc Round For Metal Parts Firing
High temperature resistance ceramic disc for metal parts firing
1.Details
1.Cordierite-Mullite kiln furniture is composed of cordierite, mullite and glass phase.
2.Due to the high temperature resistance of mullite and the low expansion of cordierite, Cordierite-Mullite kiln furniture has excellent thermal shock resistance,long service time,can be safety used at temperature below 1350℃.
3.Extruded batts are the most common type of primary kiln furniture, usually produced by semi-dry pressing, but can also be made by pressure-casting. Extruded batts can be split into ten sub-categories as follows: Extra Large Batt, Extra Thin Batt, Plain Batt, Perforated Batt, Grooved Batt,Trapezoid Batt, Recessed Batt, Full Disc, Half Disc and Special Batt.
Customer use our ceramic disc as a setter plate when firing metal parts.
2. Specification
|
Apparent porosity,%
|
28
|
|
Bulk density,g/cm3
|
2.0
|
|
Modulus of rupture, 20℃
|
≥5
|
|
1250℃×0.5h
|
≥3
|
|
Phase composition,% Mullite
|
55%
|
|
Cordierite
|
30%
|
|
Max. service temp.
|
1280 ℃
|
|
Al2O3
|
40-48%
|
|
SiO2
|
45-48%
|
|
MgO
|
5-10%
|
3. Our Service
- We will offer our best price.
- Your inquiry will be replied within 24 hours.
- Experienced staff can give you professional suggestions.
- We ensure you high quality products and timely delivery.
- We offer complete and good after-sale service.
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.