Cordierite Kiln Furniture Slabs , Porcelain Tableware Use Heat Resistant Shelf

Refractory Cordierite slab 390*370*15mm for porcelain tableware

1. Introduction 

Cordierite has excellent thermal shock resistance, good strength and can be formed by pressing, extruding, casting and vibrating into complex shapes. Cordierite mullite kiln furniture is widely used in porcelain, heavy clay, glass panel, powder metallurgy, magnetic materials, green energy, food, glass, abrasives, iron and steel, mining and aerospace engineering.
Besides its use as kiln furniture, it is also extensively used in kiln structures and kiln car system, where it is combined with ceramic fiber to achieve the aims of improving fuel efficiency and avoiding contamination.

The ideal chemistry to produce the crystals is 13.8% MgO, 34.8% Al₂O₃ and 51.4% SiO₂ (2MgO, 2Al₂O₃, 5SiO₂). Talc, kaolin and raw alumina powder can be blended to produce this chemistry (other materials are also used e.g. aluminum hydroxide, steatite and other MgO minerals). Compound materials (like kaolin and talc) react better than pure oxide materials (like MgO, Al₂O₃, SiO₂). Materials of finer particle size react better.
A simple firing to 1300C (about cone 11 and within the reach of many ordinary kilns) and soaked may produce some crystal development. However firing (actually sintering) at 1400C+ with significant soaking time is needed for the best results. Thermal expansion measuring equipment is needed to determine if your firing is actually developing the crystal matrix or not.

2. Technical Parameter 

3. Application 

Cordierite slab is widely used to sinter pottery , ceramic insulator and so on.Using temperature can not be over 1300 ℃ 

We can also supply SiSic beam.