Good creep resistance Refractory Mullite batts for high tempereature furnace

1. Description 

The ideal chemistry to produce the crystals is 65% Al₂O₃ and 33%SiO₂ . Talc, kaolin and raw alumina

powder can be blended to produce this chemistry (other materials are also used e.g. aluminum hydroxide, steatite and other MgO minerals). Compound materials (like kaolin and talc) react better than pure oxide materials (like MgO, Al₂O₃, SiO₂). Materials of finer particle size react better.

Mullite batts is widely used to sinter ceramic, powder,and so on.As noted, a continuous crystal matrix is the object of cordierite creation (not just the presence of the crystals in an otherwise typical ceramic). Notwithstanding this, cordierite powder is available, it is prefired and finely ground. It can be plasticized for forming and bonded during firing (at much lower than normal cordierite creation temperatures) to produce a ceramic that certainly has lower expansion.
 

2. Specification 

3. Features 

Our mullite batts is very strong.
Excellent energy savings
Lighter weight and higher load capacity
Excellent distortion resistance at high temperature
Suitable for faster firings with better bearing capacity for hot and cold extremes

We promise:
- We will offer our best price.
- Your inquiry will be replied within 24 hours.
- Experienced staff can give you professional suggestions.
- We ensure you high quality products and timely delivery.
- We offer complete and good after-sale service.