RAL 1011 Brown Beige Polyurethane Powder Coating For Domestic Appliances

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: 7 days

Brand: TOPO

Product Description

RAL1011 Brown beige Polyurethane powder coating for Domestic Appliances

Low temperature cure is much easier to develop in a polyester than a polyurethane powder coating. A couple caveats need to be noted. HAA polyesters are more difficult to catalyze than TGIC based polyesters. HAA polyesters can cure as low as 325°F whereas TGIC polyesters can be formulated to cure at temperatures as low as 250°F. Polyurethanes bottom-out around 300°F.

CHARACTERISTICS	1. High gloss with excellent appearance. 2. Excellent resistance to weathering with gloss retention. 3. Excellent resistance to oils, acids, alkalis and solvents. 4. Excellent hardness, adhesion and abrasion resistance.
GLOSS	Above 90%
COLOR	Desired colors
WEIGHT	Above 1.0 kg/L (Mixer)
VISCOSITY (25 °C)	60– 85 KU (Mixer)(25 °C)
DRYING TIME (25 °C)	Set-to-touch 1 hr. Dry hard 6 hrs. (25 °C).
OPTIMUM FILM THICKNESS	Wet 95μ(microns)Dry 30μ(microns)
MIXER RATIO	Base: Hardener = 2: 1 (by volume.)
NON-VOLATILE CONTENT	Above 55%
POT LIFE	4 hrs. (Mixture , 25 °C)
THINNER	PU Thinner
THINNING RATE	10~25 %
STORAGE SHELF LIFE	Minimum 1 year under normal storage conditions.
APPLICATION METHOD	Spray, Brush.
NOTE	1. Mix base and hardener according to the mixing ratio and stir thoroughly. 2. Avoid applying the paint in rain or humid weather, particularly, awet surface must be thoroughly dried. 3. All equipments must be cleaned immediately after use. 4. When used inside tanks, sufficient ventilation must be provided. 5. When overcoating interval is exceeded, paint surface must be roughened to insure adhesion. 6. Hardener can must be tightly closed to avoid reaction with moisture in air toform bubbles and gelation. 7. Strictly controlling application, not be exceed 60μ pre coat, to avoid bubbles for mation.