RAL 2005 Luminous Orange Tgic Pure Polyester Powder Coating
RAL 2005 Luminous orange polyester powder , tgic powder coating
Powder Coating you can trust TOPO! We strive to make sure your powdercoating needs are taken care and that you are happy with the process from the very start to the finish. We produce the best powder coating through the best methods and the best service standards.
Give us a try. You will be glad you did!
Product series
The products include high light ( above 86%),
glazed (76%-85%),
matt(20%-50%),
super matt (below 20%).
We also offer a variety of shiny products according to the needs of users.
Health and safety:
This product is non-toxic. In the course of inhalation of dust should be avoided. The operators should wear appropriate dust mask and glasses.
Application
Suitable for all kinds of products such as household appliances, instruments, meters medical devices,
automotive components, metal furniture, fitness equipment, indoor decorative painting, etc.
Also apply to a variety of equipment, pipes, pipe fittings and other requirements of corrosion coating.
Store below 30 °C, ventilated, dry, clean room, not near the fire, heat, direct sunlight, open dumps is prohibited.Under this condition, the powder can be stable for 12 months, more than the storage period may be re-examined, such as the results meet the requirements, can still be used.
Technic Data:
| pplication Field | Apply to anticorrosive and insulative products: | |
| Anticorrosion pipeline,rebar,bridge,steel structure, | ||
| pylon,tank,marine fittings,electric control cabinet, | ||
| switch components,lighting sets. | ||
| Application Condition | Electrostatic spray/Triboelectric gun spray. | |
| Recommended curing condition:200 degree centigrade for 12 minutes | ||
| (object surface temperature),range from 190 degree centigrade | ||
| for 20 minutes to 210 degree centigrade for 8minutes. | ||
| Recommended film thickness:50~80um, range from 40~150um | ||
| Physical Property | Specific gravity | 1.4~1.8g/cm3 as per formula and color |
| Particle size | average 35~40um | |
| Test Condition | Substrate | 0.5mm thickness cold rolled steel sheet |
| Pretreatment | Remove rust and grease | |
| Film thickness | 50~80um | |
| Curing temperature | 200 degree centigrade for 12 minutes | |
| Mechanical Property | Pencil hardness | ISO 15184:1998,2H |
| Adhesion (by griding) | GB/T 9286-1998,0grade | |
| Impact test | GB/T 1732-1993,≥50 kg.cm | |
| Bending test | GB/T 6742 ,≤2mm | |
| Cupping test | GB/T 9753,≥7mm | |
| Chemical and Durability Test | Salt spray test | GB/T 1771,≥1000 hours,no obvious change , |
| crossion width at cross≤2mm | ||
| Heat and moisture test | GB/T 1740,≥1000 hours,no change | |