DIN / EN1.4057 Martensitic Stainless Steel Pipe Large / Small Diameter SS Pipe
- Laboratory equipment
- Marine systems
- Beater bars
- Pump and propeller shafts
- Nuts and bolts
| Grade | C | Mn | Si | P | S | Cr | Ni |
|---|---|---|---|---|---|---|---|
| 1.4057 min. | - | - | - | - | - | 15 | 1.25 |
| 1.4057 max. | 0.2 | 1 | 1 | 0.04 | 0.03 | 17 | 2.5 |
| Physical Properties | Value |
|---|---|
| Density, g/cm³ (lb/in³) | 7.7 (0.278) |
| Magnetic | Yes |
| Specific heat capacity, J/(Kg·K) | 460 at 20°C (68°F) |
| Electrical resistivity, μΩ·m | 0.70 at 20°C (68°F) |
| Modulus of elasticity (Elastic Modulus), GPa (10³ ksi) | 215 (31.2) at 20°C (68°F) 212 (30.7) at 100°C (212°F) 205 (29.7) at 200°C (392°F) 200 (29) at 300°C (572°F) |
| Thermal conductivity, (W/m·K) | 25 at 20°C (68°F) |
| Mean coefficient of thermal expansion, (10⁻⁶/K) | 10.0 at 20-100°C (68-212°F) 10.5 at 20-200°C (68-392°F) 10.5 at 20-300°C (68-572°F) 10.5 at 20-400°C (68-752°F) |
Martensitic Stainless Steel: The main alloying element is chromium. Typically used in weakly corrosive media such as sea water, fresh water, and steam, with use temperatures ≤580°C. Usually employed as production materials for high-stress components and tools. Due to poor welding performance, it is generally not used as welding parts.
Through heat treatment, the mechanical properties can be adjusted. Typical grades are Cr13 type (2Cr13, 3Cr13, 4Cr13, etc.). High hardness after quenching, with different strength and toughness combinations based on tempering temperature. Mainly used in steam turbine blades, cutlery, and surgical instruments.
Austenitic Stainless Steel: The main alloying elements are chromium and nickel. This type of steel has high toughness, low brittle transition temperature, good corrosion resistance and high temperature strength, excellent oxidation resistance, and good pressure processing and welding properties.
When Cr is about 18%, Ni 8-10%, and C about 0.1%, the steel has a stable austenitic structure. Austenitic stainless steel is non-magnetic with high toughness and plasticity, but low strength. It cannot be strengthened through phase change, only by cold working. With added elements like S, Ca, Se, Te, it has good machinability.
- Coating Thickness Test
- Geometry Inspection
- Ultrasonic Inspection
- Nondestructive Testing
- Hydrostatic Testing
- Plastic caps protect both ends
- Weaving bag wrapped outside the pipe
- Packed into wooden case
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.