350mm Glossy Cigarette Thermal Lamination BOPP Film Roll For Tobacco Package
350mm Glossy Cigarette Thermal Lamination BOPP Film Roll For Tobacco Package
Introduction:
BOPP Thermal Laminating Film is mainly made of BOPP + EVA.
We use extrusion-coating process to combine these two layers.
In the final film one side has properties of BOPP film and the other side becomes heat sensitive surface used for dry lamination.
This product has two classifications: glossy/shine/transparent and matte/opaque, both of which sees thickness from 14micron to 32micron.
Its width could be from 180mm to 1880mm and length from 150m (1 inch core, 25mm) to 4000m (3 inch core, 76mm).
Its comprehensive performance is superior to moisture-proof cellophane, polyethylene (PE) film, and PET film. BOPP film also has excellent printing effects. The representative physical property data are: turbidity <1.5%; gloss> 85%; tensile strength (longitudinal / transverse)> 120 / 200MPa; elongation at break (longitudinal / transverse) <180% / 65%; elastic modulus It is 1700 ～ 2500Mpa; the embrittlement temperature is -50 ° C.
Information:
| No. | Item | Unit | Result | |
| 1 | Width bias | mm | 0 | |
| 2 | Thickness bias | % | -0.93 | |
| 3 | Average thickness bias | % | 0.64 | |
| 4 | Tensile strength | MD | Mpa | 182.6 |
| TD | 295.3 | |||
| 5 | Elongation | MD | % | 158.5 |
| TD | 59.2 | |||
| 6 | Modulus(reference value) | MD | Mpa | 2033.82 |
| 7 | Heat shrinkage | MD | % | 3.5 |
| TD | 3.9 | |||
| 8 | Haze | % | 1.72 | |
| 9 | Gloss | % | 96.2 | |
| 10 | Decaying rate of static | Treated side | 22.32 | |
| No-treated side | 20.58 | |||
| 11 | COF(q/m) | Outside/Metal | 0.218/0.146 | |
| Inside/ Metal | 0.311/0.213 | |||
Cigarette shrinkage BOPP film
1. Low Shrinkage BOPP Film
2. Middle Shrinkage BOPP Film
3. High Shrinkage BOPP Film
4. Holographic BOPP Film
5. Printed BOPP Film
Shows: