Fast-Drying Water Based Acrylic Anti-Corrosive Emulsion For Metal Coating
WL-B218 Fast-drying Acrylic Resin Corrosion Prevention Emulsion
Product Introduction
Synthetic latex WL-B218 is a fast-drying acrylic anti-corrosive emulsion synthesized by styrene-acrylic self-crosslinking process and introduced with special functional monomers.The metal anti-corrosive paint prepared with synthetic latex WL-B218 has excellent drying rate, can provide performance in a very short time, especially solves the problem of short curing time, and has excellent initial water resistance, salt water resistance and salt spray resistance, and has a certain hardness. It is easy to prepare paint, has good compatibility with pigments, fillers and powders, has good adhesion to metal substrates, and has a certain anti-flash rust effect. It is especially recommended for light and medium metal anti-corrosive paint.
Physical Property
| Polymer type | Styrene-acrylic copolymer |
| Appearance | Milky white emulsion with a slight blue luster |
| pH value (25℃) | 8±1 |
| Brookfield viscosity ( 1#/30rpm, 25℃) (cps) | 20-180 |
| Solid content (%) | 47±1 |
| Minimum film forming temperature (℃) | 55 |
| Particle diameter (μm) | 0.1-0.2 |
| Ionicity | Anionic |
Storage
The product should be stored in a sealed container and avoid freezing and high temperature. The recommended normal storage temperature is 5-35℃. The effective storage period is half a year from the date ofpackaging.
Special Tips
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.