Excellent Initial Water Resistance Epoxy Resin Combination For Automotive Axles And Chassis
WL-AD203 Epoxy resin
| Appearance | Milky white liquid |
|
Non-volatile matter (Wt, %) |
53±2 |
|
Viscosity(mPa.s)(25℃) |
500 ~ 8000 |
|
Epoxy equivalent (supplied form) (g/Eq) |
1010±50 |
WL-AD203 is a water-based epoxy dispersion. When used with the recommended water-based epoxy curing agent, it can be used to prepare high-performance water-based epoxy coatings, designed for anti-corrosion primers and epoxy floor paints for various metal substrates
Features: fast surface drying, suitable for various wet-on-wet matching processes, rapid hardness build-up, long application period
WL-AC040 Epoxy curing agent
|
Item |
Value |
Testing Method |
|
Appearance |
Light yellow transparent liquid |
Visual |
|
Non-Volatile content(%) |
40±2 |
GB/T 1725-2007 |
|
Viscosity(mPa.s)(25℃) |
2000~8000 |
GB/T 21059-2007 |
|
Active hydrogen equivalent |
300±10 |
---- |
WL-AC040 is a water-soluble modified polyamine adduct, recommended for use with waterborne epoxy resin, designed for anti-corrosion primers and epoxy floor paints for various metal substrates.
Features: fast curing speed, short surface drying time, excellent adhesion, long application period, and extremely high cost performance
WL-SP1000 is a water-based emulsion of acrylic copolymer.
Features: excellent gloss, excellent initial water resistance, good water resistance, strong versatility, suitable for primer and topcoat of various metal substrates.
|
Item |
Value |
Testing Method |
|
Appearance |
Milky white liquid |
Visual |
|
Non-Volatile content(%) |
47±1 |
GB/T1725-2007 |
|
Viscosity(mPa.s)(25℃) |
50~500 |
GB/T 21059-2007 |
|
PH |
7.0~9.0 |
GB/T 9724-2007 |
|
Minimum film forming temperature (°C) |
40 |
- |
A set of coating test data consisting of WL-AD203 epoxy/WL-AC040 curing agent primer + WL-SP1000 single component topcoat