Glass Fiber Modified Polyamide Nylon 66 Plastic Pellets PA Granules For Thermal Break Strips
Large Modulus Glass Fiber Modified Polyamide Nylon 66 Plastic Pellets PA Granules For Thermal Break Strips
Introduction of Raw Material:
PA has the advantages of high mechanical strength, high softening point, good wear resistance, self-lubrication, cushioning, sound deadening, excellent oil and chemical corrosion resistance, and good electrical insulation. Because of these superior performance, PA composite have already replaced some metals being as structural materials.
Product Description:
-PA66GF25 granules are reinforced by fiberglass. The final product performance of this raw material can meet the national standard.
-TPA66GF25 granules are based on PA66 resin. Then the granules are formed by twin-screw extrusion machine after adding fiberglass, efficient flame retardants and various additives.
Application:
Specially used in thermal break strips, thermal bridge, heat insulation bar, etc.
Polywell PA66 Granules Performance Table
| NO. | Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
| Material Properties | ||||
| 1 | Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| 2 | Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
| 3 | Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| 4 | Melting point | ºC | ≥240 | ≥240 |
| 5 | Testing for tensile cracks | - | No cracks | No cracks |
| 6 | Shore hardness | - | 80±5 | 80-85 |
| 7 | Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| 8 | Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| 9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
| 10 | Elongation at break | % | ≥2.5 | ≥2.6 |
| 11 | Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| 12 | High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| 13 | Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| 14 | Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| 15 | Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
Advantage:
-
high mechanical strength
-
high toughness
-
high softening point
-
good wear resistance
-
self-lubrication
-
long-term work at higher temperatures
-
It has high CTI value , excellent electrical insulation , low smoke and low toxicity characteristics.
Packaging & Delivery:
Packaging details:25kg/bag
Delivery details: shipped in 5-8 working days after receiving the payment
Please feel free to contact us if you have any questions.