Cut to size AZ31B Magnesium tooling plate, polished surface with fine flatness
Xi'an Yuechen Metal Products Co., Ltd. is a major magnesium alloy materials manufacturer with the ability to supply magnesium alloy plate, magnesium tooling plate, AZ31B-TP tooling plate, magnesium alloy sheet, Magnesium CNC engraving plate, Magnesium CNC engraving sheet, Magnesium tooling sheet, Magnesium extrusions, Cast magnesium tooling plate, magnesium alloy rod, magnesium alloy billet, magnesium alloy bar, magnesium welding rod, magnesium welding wire, magnesium flat bar, magnesium coil, magnesium alloy ingot, Mg-RE (magnesium rare earth) alloy ingot, etc. in both large and small quantities. There is no order that is too large or too small. We provide the same level of service and attention to detail to all of your magnesium alloy materials’ needs. In addition to exceptional service, you will get only the highest quality magnesium alloy materials at XYMCO. All of our products meet stringent AMS and ASTM standards including AMS 4375, AMS 4376, AMS 4387, AMS 4383, AMS 4388, AMS 4389, AMS 4390, AMS 4384, AMS 4385, AMS 4350, AMS 4360, AMS 4362, AMS4377G, ASTM B90/B90M-15, MIL-DTL 32333, MIL-T-38749, QQ-M-44B, ASTM B107/B107M-13 and ASTM B91-97
AZ31B is a wrought magnesium base alloy with good room-temperature strength and ductility combined with corrosion resistance and weldability. Increased strength is obtained by strain hardening with a subsequent partial anneal (H24 and H26 tempers). Our sheet and plate’s size range is:
Sheet: thickness from 0.5mm to 6mm; Max. width is 600mm; Max. length is 6000mm;
Plate: thickness from 6 mm to 200mm; Max. width is 2000mm; Max. length is 6000mm;
Block: We can supply precut blocks according to customer’s requirements.
APPLICATIONS
Sheet and plate in AZ31B find application in medium strength service at temperatures below 150°C. Diverse uses including aerospace, aircraft, concrete tools, 3C (cell phone / camera / computer), speaker cones and textile machinery can all benefit from light weight AZ31B.
AZ31B is non-magnetic and has high electrical and thermal conductivity filling the requirements for RFI and EMI shielding in the electronics and computer industries.
Superplastic forming of AZ31B sheet at elevated temperatures allows production of a wide variety of intricate parts for automotive uses. Monocoque construction utilizing formed sheet can be adapted to many commercial applications.
SPECIFICATIONS
ASTM B90/B90M-07
AMS 4375
AMS 4376
AMS 4377
CHEMICAL COMPOSITION
Al: 2.5-3.5%
Zn: 0.7-1.3%
Mn: 0.20 – 1.0%
Mg: Balance
PHYSICAL PROPERTIES
Density: 1.78
Coefficient of thermal expansion: 26.8 x 10-6K-1
Specific heat: 1040 Jkg-1k-1
Thermal conductivity: 76.9Wm-1k-1
Electrical resistivity: 92nΩm
Modulus of elasticity: 45 x 109Pa
Poissons ratio: 0.35
Melting range: 566 - 632°C
HEAT TREATMENT
No thermal treatment is available for increasing the strength of this alloy after fabrication.
MECHANICAL PROPERTIES
| Alloy and Temper | Thickness (mm) |
Yield Strength 0.2% offset (MPa) |
Tensile strength (MPa) |
Elongation In 5.65 √A (%) |
| AZ31B-O | 0.5 – 1.5 | 125 | 221 | 10 |
| 1.5 – 6.3 | 105 | 221 | 9 | |
| 6.3 - 75 | 105 | 221 | 8 | |
| AZ31B-H24 | 0.5 – 6.3 | 200 | 269 | 5 |
| 6.3 -9.5 | 179 | 262 | 7 | |
| 9.5 – 12.7 | 165 | 255 | 8 | |
| 12.7 - 25 | 152 | 248 | 8 | |
| 25- 50 | 138 | 234 | 6 | |
| 50 - 80 | 124 | 234 | 7 | |
| AZ31B-H26 | 6.3 - 10 | 186 | 269 | 6 |
| 10 – 12.5 | 179 | 262 | 6 | |
| 12.5 - 20 | 172 | 255 | 5 | |
| 20 – 25 | 159 | 255 | 5 | |
| 25 - 40 | 152 | 241 | 5 | |
| 40 - 50 | 148 | 241 | 5 |
The sheet and plate shall conform to the tensile requirements in above Table unless other agreement is made between seller and purchaser. Mechanical Properties for sizes and tempers not shown in above Table shall be as agreed upon by seller and purchaser.
OTHER PROPERTIES
Typical Hadness
O temper: 67 Rockwell E
H24 temper: 83 Rockwell E
WELDABILITY
Excellent weldability with gas shielded arc using AZ61A (preferred) or AZ92A filler rod; post weld stress relief is required to prevent stress corrosion cracking. Resistance welding is excellent.
MACHINING
AZ31B, like all magnesium alloy sheet and plate, machines faster than any other metal. Providing the geometry of the part allows, the limiting factor is the power and speed of the machine rather than the quality of the tool material. The power required per cubic centimeter of metal removed varies from 9 to 14 watts per minute depending on machining operation.
DENT RESISTANCE
Weight for weight, AZ31B-H24 has proven to be superior to competitive materials in its resistance to denting at moderate energy levels.
Dent Resistance of 1mm Gauge Sheet (Dent depth in mm from 25mm spherical redius indentor on 350mm span)
| Impact Energy 0.34 J | Impact Energy 0.62 J | Impact Energy 1.25 J | |
|
AZ21B-H24 6061 – T6 3003 – H14 5052 – H34 2024 – T6 SAE 1010 Mild Steel |
0.66 0.94 2.24 1.55 0.99 1.09 |
1.42 1.52 3.23 2.41 1.52 1.70 |
2.34 2.46 4.90 3.35 2.29 2.67 |
SURFACE TREATMENT
All the normal chromating, anodizing, plating, and finishing treatment are readily applicable. AZ31B also responds well to plasma electrolytic oxidation finishing.
CORROSION RESISTANCE
Continuous exposure for 2.5 years.
Marine Atmosphere
AZ31B-H24 0.008mg.cm-2d-1
Mild steel 0.323mg.cm-2d-1
Industrial Atmosphere
AZ31B-H24 0.013mg.cm-2d-1
Mild steel 0.055mg.cm-2d-1
Rural Atmosphere
AZ31B-H24 0.006mg.cm-2d-1
Mild steel 0.032mg.cm-2d-1