2.78 G/Cc Density 2024 Aluminium Seamless Pipe With Corrosion Resistance

Price Negotiable

Price: Negotiable

MOQ: 1METRIC TONS

Delivery Time: 30 days

Brand: HUANYU

Product Description

6M Long Corrosion Resistance 2024 Seamless Aluminum Tubing With High Strength

Diameter: 32mm

Wall Thickness: 7mm

Length: 6meters

Availability: 300 metric tons per month

2024 seamless aluminum tubing

is heavily utilized in aircraft applications due to good machining characteristics and higher strength than either 2014 or 2017. Cold formability is considered fair, yet it is one of the most popular alloys for high strength tubing requirements because of the superior grain structure that can be obtained.

Physical Properties

	Metric	English	Comments

Density	2.78 g/cc	0.1 lb/in³	AA; Typical
Mechanical Properties

Hardness, Brinell	47	47	AA; Typical; 500 g load; 10 mm ball
Ultimate Tensile Strength	186 MPa	27000 psi	AA; Typical
Tensile Yield Strength	75.8 MPa	11000 psi	AA; Typical
Elongation at Break	20 %	20 %	AA; Typical; 1/16 in. (1.6 mm) Thickness
Elongation at Break	22 %	22 %	AA; Typical; 1/2 in. (12.7 mm) Diameter
Modulus of Elasticity	73.1 GPa	10600 ksi	AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus.
Ultimate Bearing Strength	345 MPa	50000 psi	Edge distance/pin diameter = 2.0
Bearing Yield Strength	131 MPa	19000 psi	Edge distance/pin diameter = 2.0
Poisson's Ratio	0.33	0.33
Fatigue Strength	89.6 MPa	13000 psi	AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen
Machinability	30 %	30 %	0-100 Scale of Aluminum Alloys
Shear Modulus	28 GPa	4060 ksi
Shear Strength	124 MPa	18000 psi	AA; Typical
Electrical Properties

Electrical Resistivity	3.49e-006 ohm-cm	3.49e-006 ohm-cm	AA; Typical at 68 Degrees F
Thermal Properties

CTE, linear 68 Degrees F	23.2 µm/m- Degrees C	12.9 µin/in- Degrees F	AA; Typical; Average over 68-212 Degrees F range.
CTE, linear 250 Degrees C	24.7 µm/m- Degrees C	13.7 µin/in- Degrees F	Average over the range 20-300 Degrees C
Heat Capacity	0.875 J/g- Degrees C	0.209 BTU/lb- Degrees F
Thermal Conductivity	193 W/m-K	1340 BTU-in/hr-ft²- Degrees F	AA; Typical at 77 Degrees F
Melting Point	502 - 638 Degrees C	935 - 1180 Degrees F	AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater. Eutectic melting is not eliminated by homogenization.
Solidus	502 Degrees C	935 Degrees F	AA; Typical
Liquidus	638 Degrees C	1180 Degrees F	AA; Typical
Processing Properties

Annealing Temperature	413 Degrees C	775 Degrees F
Solution Temperature	256 Degrees C	493 Degrees F