90WNiFe High Hardness Tungsten Alloy Pins With Wearing Resistance

Tungsten Alloy Pins are made of tungsten base (tungsten content is generally 80% - 98%) and a small amount of nickel, iron, copper, cobalt, molybdenum, chromium and other elements. The density of high specific gravity tungsten alloy can reach 15.20 ~ 18.70g/cm3, also known as high specific gravity tungsten alloy or high density alloy material. Because the weight of tungsten alloy is more than twice that of steel.

Introduction and Feature of Tungsten Alloy Pins

Tungsten alloy has a series of excellent properties, high specific gravity: General specific gravity 16.5-18.75g/cm3, high strength: tensile strength 700-1000mpa, light absorption strength: 30-40% higher than general lead specific gravity, high thermal conductivity: the mold is 5 times that of steel; Low thermal expansion coefficient: the capacity is only 1 / 2 / 3 of that of steel, and the resistance to conduction, welding and cutting is good.
A common method for making heavy tungsten alloys is to mix the desired tungsten, iron, nickel or copper powders and then cold-press the liquid phase to near full density. During the liquid phase treatment, the base tungsten alloy is melted, and part of the tungsten enters the solution, forming a microstructure of large tungsten particles (20-60 m) dispersed in the base alloy.

SPECIFICATIONS of Tungsten Alloy Pins

Chemical Composition	90%W			93%W			95%W		97%W
State	Sinter	Vacuum	Forge	Sinter	Vacuum	Forge	Sinter	Vacuum	Sinter	Vacuum
Density (g/cc)	16.85-17.25			17.15-17.85			17.75-18.35		18.25- 18.85
Hardness (HRC)	32 Max	30 Max	40 Min	33 Max	31 Max	40 Min	34 Max	32 Max	35 Max	33 Max
Tensile Strength (Max)	770 Min	900 Min	1400 Max	770 Min	910 Min	1440 Max	735 Min	920 Min	700 Min	850 Min
Yield Strength (Mpa)	620 Min	620 Min	1280 Max	650 Min	650 Min	1340 Max	650 Min	650 Min	-	-
Elongation (%)	5 Min	15 Min	5 Min	5 Min	12 Min	3 Min	3 Min	12 Min	2 Min	6 Min

Tungsten Alloy Pins Picture:

Application of Tungsten Alloy Pins

Tungsten Alloy Pins are made of high gravity tungsten alloy. The wear resistance, hardness, strength and heat resistance of the alloy are further improved, and the consistency of the products is better ensured. Because of these characteristics, tungsten iridium holes have become an important part of the high-tech crystal glass industry.