NAS630 S17400 Stainless Steel Shaft Stock Precipitation Hardened Microstructure
NAS630 S17400 Stainless Steel Shaft Stock Precipitation Hardened Microstructure
NAS630 S17400 17-4PH precipitation hardened stainless steel Shaft stock
The NAS630 S17400 17-4PH alloy is a precipitation, quenched, martensitic stainless steel, and this grade has high strength, hardness (up to 300 0 C / 5000 C) and corrosion resistance. After heat treatment, the mechanical properties of the product are more complete, and it can reach compressive strength of up to 1100-1300 mpa (160-190 ksi). This grade cannot be used above 300 0C (572 0F) or very low temperature. It has good corrosion resistance to the atmosphere and diluted acids or salts. It has the same corrosion resistance as 304 and 430.
|
3/16" |
1/4" |
5/16" |
3/8" |
7/16" |
1/2" |
9/16" |
5/8" |
3/4" |
7/8" |
1" |
|---|---|---|---|---|---|---|---|---|---|---|
|
4.8mm |
6.3mm |
7.9mm |
9.5mm |
11.1mm |
12.7mm |
14.3mm |
15.9mm |
19mm |
22.2mm |
25.4mm |
|
|
||||||||||
|
1 1/8" |
1 1/4" |
1 1/2" |
1 3/4" |
2" |
2 1/4" |
2 1/2" |
2 3/4" |
3" |
3 1/2" |
4" |
|
28.6mm |
31.8mm |
38.1mm |
44.5mm |
50.8mm |
57.2mm |
63.5mm |
69.9mm |
76.2mm |
88.9mm |
101.6mm |
Application area:
Offshore platforms, helicopter decks, other platforms
food industry
Pulp and paper industry
Aerospace (turbine blades)
mechanical part
Nuclear waste barrel
chemical composition:
|
C |
Cr |
Ni |
Cu |
Nb/Cb |
Mn |
|---|---|---|---|---|---|
|
0.04 |
16.5 |
4.5 |
3.3 |
0.3 |
0.7 |
|
PREN (%Cr+3.3%Mo+16%N)≥17 |
|||||
Mechanical properties
|
Hardened |
YS 0.2% |
UTS |
||
|---|---|---|---|---|
|
Min. |
Typ. |
Min. |
Typ. |
|
|
A |
1070 |
1207 |
1170 |
1310 |
|
B |
790 |
931 |
965 |
1034 |
|
Hardened |
YS 0.2% |
UTS |
|
El% |
|||
|---|---|---|---|---|---|---|---|
|
Min. |
Typ. |
Min. |
Typ. |
|
Min. |
Typ. |
|
|
A |
155 |
175 |
170 |
190 |
|
8 |
14 |
|
B |
115 |
135 |
140 |
150 |
|
10 |
17 |
Hardened at 496 ° C (925 ° F)-4 hours-air cooled
Hardened 593 ° C (1100 ° F)-4 hours-air cooled
The above are two examples of heat treatment.
NAS630 S17400 17-4PH precipitation hardened stainless steel Shaft
Hardness/Temperature tempered for 4 hours after austenitizing at 1040°C (1904°F) for 30 min quenched 100°C/sec (212°F/sec).