2.4816 Inconel 600 Tube Blank For Pipeline Flue Gas Emission Reduction Project Of Super Centrifuge

2.4816 Inconel 600 Tube Blank

Material designation:

Inconel 600 nickel based alloy

US grade: N06600 / NS3102

Inconel 600 (N06600) nickel-based alloy process performance and requirements:

1. Inconel600 formability: The alloy has good hot workability. The heating temperature of ingot forging is 1110 ～ 1140 ℃; the final forging temperature is not less than 950 ℃, the slab rolling heating temperature is 1130 ～ 1170 ℃, and the finishing rolling heating temperature is 1090 ~ 1130 ° C. The final solution treatment temperature is 1010 to 1050 ° C.

2. Inconel600 welding performance: alloy welding performance is good, can be connected by various methods such as arc welding, argon arc welding, resistance welding and brazing, large or complex welded structural parts should be annealed at 870 ℃ for 1h after welding to eliminate Welding stress.

3. Inconel600 parts heat treatment process: The heat treatment process of parts should be performed according to the corresponding material standard heat treatment system. Annealing of sheet and strip parts should be performed in a protective atmosphere.

Inconel 600 (N06600) nickel-based alloy chemical composition: see Table-1:

Table-1                                                                                    %

Note: 1 Standard BZ-44-9003B-0 for aerospace materials specifies ω (C) ≤ 0.10%, ω (P) ≤ 0.020%, and ω (Nb) ≤ 1.00%.

specification:

Outer diameter Φ6—762mm; wall thickness: 0.5-50mm, maximum length 18000mm
Special specifications are available upon negotiation.