Windmill Blade Putty - Polyaspartic Coating Formulation
Windmill Blade Putty - Polyaspartic Coating Formulation
Curing method
Air-drying.
Application
Fiberglass substrate windmill blade putty.
Characters
No VOC, fast cure, good flexibility, good grinding performance, good compatibility with epoxy.
A Component
| Material | Content |
| F524 | 21.5 |
| F330 | 3 |
| dispersing agent | 1 |
| titanium dioxide | 10 |
| barium sulfate | 25 |
| 3A molecular sieve | 4.5 |
| calcium carbonate | 22.9 |
| talcum powder | 10 |
| Grind to fineness≤70um | |
| Silane coupling agent | 1.5 |
| Defoamer | 0.5 |
| Leveling agent | 0.1 |
B Component
| Material | Content |
| Tolonate HDT | 20 |
| GB808A-100 | 80 |
Ratio
A:B = 5 :1
Specifications
| Pot life | 10m | |
| TVOC, g/L | ≤20 | |
| Touch dry time | 0.5h | |
| Hard dry time | 4h | |
| Hardness | HB | |
| Elongation | 50% | |
| Adhesion,MPa | ≥12 | |
Feiyang Protech has been specializing in the production of raw materials for polyaspartic coatings for 30 years and can provide polyaspartic resins, hardeners and coating formulations. Feel free to contact us: marketing@feiyang.com.cn, feiyangjunyan@gmail.com
Our products list:
Polyaspartic Coating Formulation showcase cases - Consult our engineers to customize a coating formulation for your project. Contact our Tech Team
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.