"Zheheng steel" is a professional manufacturer of 1.4583 320S18 X6CrNiMoTi17-12-2 316Ti stainless steel pipe fittings and flanges, the main products are stainless steel pipe, stainless steel pipe fittings (stainless steel elbow, stainless steel tee, stainless steel flange, stainless steel reducing pipe, 

Technical specifications of W-Nr 1.4583 austenitic stainless steel - Chemical composition,mechanical properties from steelmaking,forging,rolling,heat treatment,cold working.We also possess advanced precision machining equipments for further processing
CHEMICAL COMPOSITION (WEIGHT %)
C(％): ≤0.10
Si(％)≤: 1.00
Mn(％)≤: 2.00
P(％)≤: 0.045
S(％)≤: 0.030
Cr(％): 12.0～14.5
Ni(％): 12.0～14.5
Mo(％): 2.50～3.00
Other(％): Nb≥8×C％

MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) UNDER ROOM TEMPERATURE
Condition: quenched
Thickness/mm: -
σb/MPa: 490~740
σ0.2≥/MPa: 220
δ5≥(％): 40
ψ≥(％): 50
Akv≥/J: 55
Hardness HBS30: 190 ~ 230

MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM TEMPERATURE
Hot forming temp/℃: 1150~750
Heat treatment temperature and cooling methods|annealing: -
Heat treatment temperature and cooling methods|quenching: 1050~1100 water/air cooled
Heat treatment temperature and cooling methods|tempering: -
Condition: quenched
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100: 191
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200: 162
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300: 157
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400: 149
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500: 137

products description

Equivalent steels for grade 10KH17N13M2T ( 10Х17Н13М2Т ) ,1.4583