Low Free TDl/Polyether Prepolymer Equivalent To Adiprene LF 1950A

1. Description

LFE1595 based on TDI-Polyester, it has lower viscosity, longer pot life and faster demolding with a range curatives to enable high productivity. The elastomer has good low temperature flexibility, excellent dynamic properties and outstanding abrasion resistance.

Properties	Typical Value
NCO Content, %	5.6 ± 0.2
Appearance, 25℃	Solid
Viscosity, 90℃,cps	750
Processing Conditions	Prepolymer	Moca
Temperature,℃	90	115
Mix ratio by weight	100	17
Pot Life,min	8
Demold ℃/Minutes	110/30
Post Cure, ℃/Hrs.	110/15

2. Typical Physical Properties

Properties	Method	Units	Typical Value
Hardness	ASTM D 2240	Shore A	95 ± 2
Tensile Strength	ASTM D 412	MPa	55
Elongation at Break	ASTM D 412	%	440
100% Modulus	ASTM D 412	MPa	14.7
300% Modulus	ASTM D 412	MPa	29.6
Rebound, Bayshore	ASTM D 2632	%	34
DIN Abrasion	DIN 53516	mm³	52
Tear Strength	ASTM D 624	kN/m	135
Compression Set B (70°C, 22hrs)	ASTM D 395	%	32