High-End PVC Coated Film for Bank Card Lamination - 0.04-0.10mm Thickness, ≥6.0 N/cm Peel Strength
High-end PVC coated overlay film specifically engineered for financial bank card lamination applications. This premium film delivers exceptional performance characteristics including superior adhesion, extended aging life, and minimal color change or shrinkage after lamination.
- Strong initial viscous force with slow decline rate
- Excellent yellowing resistance properties
- Superior deformation resistance after laminating
- Smooth surface for easy application and handling
- High peeling strength with long aging time
- Minimal color change and shrinkage ratio
| Parameter | Value |
|---|---|
| Vicat Softening Point | 72±2 ℃ |
| Heating Shrinkage Ratio | ≤ 10% |
| Tensile Strength | ≥ 40 MPa |
| Normal Thickness | 0.04, 0.05, 0.06, 0.08, 0.10 mm |
| Peel Strength (90°, 300mm/min) | ≥ 6.0 N/cm |
| Aging Time (65℃ temp./95% humidity) | >200 hours |
| Suitable Ink Types | Offset and silk screen printing UV ink, pigment and dye ink for inkjet printing, digital printing ink |
- Size Options: Available in reel or sheet formats including A4, A3, or custom requirements
- Thickness: 0.04, 0.05, 0.06, 0.08, 0.10 mm
- Color: Transparent with one-side glue coating
- Packaging: By reel or 500 sheets per bag / 4-8 bags per paper carton, or custom requirements
Store sealed in moisture-proof conditions at room temperature under 40℃. Keep horizontally, avoid heavy pressing and direct sunlight exposure.
Ideal for protective film applications on bank cards, social security cards, IC cards, RF cards, and other high-requirement card products. MCO-W model is compatible with most PVC sheets printed by various printers and applicable to almost all sheets printed by different ink types.