17x5.6×0.7mm Non Standard Parts Cemented Carbide Tips For Surgical Needle Holder
High Performance Cemented Carbide Tips For Surgical Needle Holder, Medical Needle Holder TC Inserts
1.High wear resistance
2.long lifetime
3.good price
4.short delivery time
5.High quality
Performance chart:
| Grade | Cobalt content | Binder | WC particle /grain size |
Density | Hardness | Coercive force Coercivity HC |
Transverse Rupture Strength Flexural strength |
||
| (wt%) | (%) | (μm) | (g/cm3) | HRA | HV10 | HV30 | (KA/m) | (MPa) or (N/mm2) | |
| STK3050 | 8.6-10.0 | 10 | 5.0 | 14.53 | 86.30 | 1010 | 4.0-5.0 | 2650 | |
| YL2 | 7.0-8.2 | 8.2 | ≤1.0 | 14.75 | 91.50 | 1530 | 17.0-19.0 | 3000 | |
| YL3 | 6.8-8.2 | 8.2 | ≤1.0 | 14.70 | 91.50 | 1530 | 17.0-20.0 | 2800 | |
| YL10 | 8.5-10.0 | 10 | 1.2 | 14.48 | 90.50 | 1410 | 12.5-15.5 | 3100 | |
| YG6 | 14.85 | 90.00 | 2000 | ||||||
| YG8E | 7.0-8.2 | 8.3 | 1.6 | 14.60 | 89.80 | 1330 | 10.0-14.0 | 2600 |
|
Production and test:
1)The carbide tips will start to prepare the powder as per the customer’s requirement with our wet-grinding machine
2) Before mass production, we need to do a trial pressing and sintering, and we check the appearances and the sizes of the samples with a micrometer to ensure that the requirements of the drawings can be met before batch production
3) Bulk production, press the raw materials to shape blanks, and carbide tips must be passed by semi-finished inspection.
4) sinter blanks to finish (HIP) and finished products inspection to ensure the best quality and production capacity.