3000 series high quality aluminum circle for kitchenware H14

Price Negotiable

Price: Negotiable

MOQ: 1 Ton

Delivery Time: 7-20 Days

Brand: Henan Yongsheng

Product Description

3000 Series High Quality Aluminum Circle for Kitchenware H14

Product Specifications

Product Features

Lightweight and Strength Balance: Our aluminum discs with a density of just 2.73 g/cm³, it is 66% lighter than stainless steel, giving kitchenware a lightweight design. This not only reduces transportation costs but also significantly reduces the weight of kitchenware, making single-handed operation more effortless. The manganese (Mn) reinforcement achieves a tensile strength of 150-220 MPa. For example, a wok can withstand 100,000 stir-fries without deformation.
Excellent Thermal Conductivity: The 3000 series aluminium has a thermal conductivity of up to 135 W/(m*K). As kitchenware, it heats up three times faster than stainless steel and saves 15% energy.
Food-grade corrosion resistance: The food-grade corrosion resistance of 3000 series aluminium meets food safety standards such as FDA, GB 4806.9, and LFGB. The natural oxide film and manganese (Mn) elements work synergistically to ensure no perforation after 500 hours of salt spray testing.
Exceptional plastic deformation capability: 3000 series aluminium in the H24 condition maintains an elongation rate of 8-12%, balancing strength and formability. It can easily achieve complex processes such as deep drawing and spinning. 3003 aluminium circle plates can achieve a depth-to-diameter ratio of 1:1.5.

Technical Parameters

Parameter	Specification
Product Name	Aluminum Circle / Aluminum Disc
Standard	GB/T3880, ASTM, B209
Series	1050, 1060, 1070, 1100, 3003, 3004, 3105, 5052, 5754 etc.
Temper	O,H12,H14,H16,H18,H24,H32,etc
Process	Hot rolled (DC) or Cold rolled (CC)
Thickness	0.13-6.5mm or customized
Diameter	80mm -1000mm or customized
Tolerance	±1%
MOQ	1 Ton
Sample	1-2 pieces of free samples available
Appearance	Flat, clean surface without scratches, cutting edge no burrs

Chemical Composition (%)

Grade	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Al
1050	0.25	0.4	0.05	0.05	0.05	-	0.05	0.03	99.5
1060	0.25	0.35	0.05	0.03	0.03	-	0.05	0.03
1070	0.2	0.25	0.04	0.03	0.03	-	0.04	0.03	99.6
1100	Si+Fe:0.95	0.05-0.4	0.05	-	-	0.1	-		99.7
3003	0.6	0.7	0.05-0.2	1.0-1.5	-	-	0.1	-	99
3004	0.3	0.7	0.25	1.0-	0.8	-	0.25	-	remains
3005	0.6	0.7	0.3	1.0-1.5	0.2-0.6	0.1	0.25	0.1	remains
3105	0.6	0.7	0.3	0.3-0.8	0.2-0.8	0.2	0.4	0.1	remains
5052	0.25	0.4	0.1	0.1	2.2-2.8	0.15-0.35	0.1	-	remains
5083	0.4	0.4	0.1	0.4-1.0	4.0-4.9	0.05-0.25	0.25	0.15	remains
5086	0.4	0.5	0.1	0.2-0.7	3.5-4.5	0.05-0.25	0.25	0.15	remains
6061	0.4-0.8	0.7	0.15-0.4	0.15	0.8-1.2	0.04-0.35	0.25	0.15	remains
6063	0.2-0.6	0.35	0.1	0.1	0.45-0.9	0.1	0.1	0.1	remains