High Strength Fast Drying SiC Castable For Steel Plants Iron Runner refractory castable material
Fast Drying SiC Castable For Steel Plants Iron Runner
Fast Drying Castable for Iron Notch is made of corundum, high quality bauxite and silicon carbide incorporated with appropriate drying agent. By firing 2 to 3 hours, the products can be put into use, and show excellent performance. Fast Drying Castable for Iron Notch overcomes the shortcomings of ramming mixes such as short service life, frequent maintenance, high materials consumption and high labor intensity, as well as the shortcomings of normal castables such as long time firing.
Fast Drying Castable for Iron Notch has been widely applied at iron runner, slag trough and gain good performance.
|
Product code |
CH-TGKJ-70 |
CH-TGKJ-65A |
CH-TGKJ-65 |
CH-TGKJ-60 |
|
Al2O3/% |
70 |
65 |
65 |
60 |
|
SIC+C% |
15 |
20 |
8 |
20 |
|
Bulk density/g.cm3 |
2.8(110℃24h) |
2.8(110℃24h) |
2.85(110℃24h) |
2.7(110℃24h) |
|
Cold crushing strength/Mpa |
3(110℃24h) |
3(110℃24h) |
5(110℃24h) |
3(110℃24h) |
|
5(1450℃3h) |
5(1450℃3h) |
8(1450℃3h) |
5(1450℃3h) |
|
|
Modulus of rupture/MPa |
20(110℃24h) |
20(110℃24h) |
20(110℃24h) |
20(110℃24h) |
|
30(1450℃3h) |
30(1450℃3h) |
30(1450℃3h) |
30(1450℃3h) |
|
|
Permanent linear change／％ |
0.8(1450,3h) |
0.8(1450,3h) |
0.8(1450,3h) |
0.8(1450,3h) |
|
Application |
iron runner, slag runner |
Slag line of iron runner |
Branch of iron runner |
Slag runner |